Solvay Specialty Polymers Ixef® 1524 Polyarylamide (PARA) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyarylamide (PAA) , Polyarylamide, Glass Fiber Filled
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Ixef® 1524 Polyarylamide (PARA) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ixef 1524 is a 50% glass-fiber reinforced, halogen-free flame retardant polyarylamide which exhibits high strength and stiffness, good surface gloss, and excellent creep resistance. - Black: Ixef 1524/9008 - Custom ColorableInjection Notes: Hot Runners: 250°C to 260°C (482°F to 500°F) Injection Pressure: rapid Drying This resin should be dried to a target moisture content of less than 0.10%. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 1-2 hours at 120°C (248°F), 2-4 hours at 100°C (212°F), or 2-8 hours at 80°C (176°F). Injection Molding IXEF 1524 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The measured melt temperature should be about 270°C (518°F), and the barrel temperatures should be around 250°C to 260°C (482°F to 500°F) in the rear zone, gradually increasing to 260°C to 275°C (500°F to 527°F) in the front zone. If hot runners are used, they should be set to 250°C to 260°C (482°F to 500°F). To maximize crystallinity, the temperature of the mold cavity surface must be held between 120°C and 140°C (248°F and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95%-99%).Data is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.68 g/cc	0.0607 lb/in³	ISO 1183
Filler Content	50 %	50 %	Glass Fiber Reinforcement
Water Absorption	0.30 % @Temperature 23.0 °C, Time 86400 sec	0.30 % @Temperature 73.4 °F, Time 24.0 hour	ISO 62
Moisture Absorption at Equilibrium	1.0 %	1.0 %	65% RH; Internal Method
	1.3 %	1.3 %	65% RH; Internal Method
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	Internal Method

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	230 MPa	33400 psi	ISO 527-2
Elongation at Break	1.9 %	1.9 %	ISO 527-2
Tensile Modulus	20.0 GPa	2900 ksi	ISO 527-2
Flexural Strength	240 MPa	34800 psi	Conditioned; ISO 178
	330 MPa	47900 psi	ISO 178
Flexural Modulus	15.5 GPa	2250 ksi	Conditioned; ISO 178
	18.5 GPa	2680 ksi	ISO 178
Charpy Impact Unnotched	4.80 J/cm²	22.8 ft-lb/in²	ISO 179/1eU
Charpy Impact, Notched	0.930 J/cm²	4.43 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	227 °C	441 °F	Unannealed; ISO 75-2/A
Flammability, UL94	V-0 @Thickness 0.400 mm	V-0 @Thickness 0.0157 in	All Colors; UL 94
Oxygen Index	37 %	37 %	ISO 4589-2
Glow Wire Test	775 °C @Thickness 0.400 mm	1430 °F @Thickness 0.0157 in	Glow Wire Ignition Temperature; IEC 60695-2-13
	800 °C @Thickness 0.750 mm	1470 °F @Thickness 0.0295 in	Glow Wire Ignition Temperature; IEC 60695-2-13
	825 °C @Thickness 1.50 mm	1520 °F @Thickness 0.0591 in	Glow Wire Ignition Temperature; IEC 60695-2-13
	850 °C @Thickness 3.00 mm	1560 °F @Thickness 0.118 in	Glow Wire Ignition Temperature; IEC 60695-2-13

Electrical Properties	Metric	English	Comments
Dielectric Constant	4.44 @Frequency 2.40e+9 Hz	4.44 @Frequency 2.40e+9 Hz	Method B; ASTM D2520
Dissipation Factor	0.012 @Frequency 2.40e+9 Hz	0.012 @Frequency 2.40e+9 Hz	Method B; ASTM D2520
High Voltage Arc Resistance to Ignition (HVAR)	>= 300 sec @Thickness 3.00 mm	>= 300 sec @Thickness 0.118 in	PLC 0; UL 746
Comparative Tracking Index	>= 600 V	>= 600 V	IEC 60112
	>= 600 V @Thickness 3.00 mm	>= 600 V @Thickness 0.118 in	UL 746
	>= 600 V @Thickness 3.00 mm	>= 600 V @Thickness 0.118 in	PLC 0; UL 746
Hot Wire Ignition, HWI	60 - 120 sec @Thickness 0.400 mm	60 - 120 sec @Thickness 0.0157 in	PLC 1; UL 746
	95 sec @Thickness 0.400 mm	95 sec @Thickness 0.0157 in	UL 746
	>= 120 sec @Thickness 0.750 mm	>= 120 sec @Thickness 0.0295 in	UL 746
	>= 120 sec @Thickness 0.750 mm	>= 120 sec @Thickness 0.0295 in	PLC 0; UL 746
	>= 120 sec @Thickness 1.50 mm	>= 120 sec @Thickness 0.0591 in	UL 746
	>= 120 sec @Thickness 1.50 mm	>= 120 sec @Thickness 0.0591 in	PLC 0; UL 746
	>= 120 sec @Thickness 3.00 mm	>= 120 sec @Thickness 0.118 in	UL 746
	>= 120 sec @Thickness 3.00 mm	>= 120 sec @Thickness 0.118 in	PLC 0; UL 746
High Amp Arc Ignition, HAI	37.6 arcs @Thickness 0.400 mm	37.6 arcs @Thickness 0.0157 in	UL 746
	30 - 60 arcs @Thickness 0.400 mm	30 - 60 arcs @Thickness 0.0157 in	PLC 2; UL 746
	30 - 60 arcs @Thickness 0.750 mm	30 - 60 arcs @Thickness 0.0295 in	PLC 2; UL 746
	53.6 arcs @Thickness 0.750 mm	53.6 arcs @Thickness 0.0295 in	UL 746
	70.2 arcs @Thickness 1.50 mm	70.2 arcs @Thickness 0.0591 in	UL 746
	60 - 120 arcs @Thickness 1.50 mm	60 - 120 arcs @Thickness 0.0591 in	PLC 1; UL 746
	60 - 120 arcs @Thickness 3.00 mm	60 - 120 arcs @Thickness 0.118 in	PLC 1; UL 746
	95.4 arcs @Thickness 3.00 mm	95.4 arcs @Thickness 0.118 in	UL 746
High Voltage Arc-Tracking Rate, HVTR	0.000 - 10.0 mm/min @Thickness 3.00 mm	0.000 - 0.394 in/min @Thickness 0.118 in	PLC 0; UL 746

Processing Properties	Metric	English
Rear Barrel Temperature	250 - 260 °C	482 - 500 °F
Front Barrel Temperature	260 - 290 °C	500 - 554 °F
Melt Temperature	280 °C	536 °F
Mold Temperature	120 - 140 °C	248 - 284 °F
Drying Temperature	100 °C	212 °F
Dry Time	1.00 - 3.00 hour	1.00 - 3.00 hour

Descriptive Properties	Value	Comments
Additive	Flame Retardant
Appearance	Black
	Colors Available
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Bromine Free
	Flame Retardant
	Good Chemical Resistance
	Good Creep Resistance
	Good Dimensional Stability
	Halogen Free
	High Flow
	High Strength
	Low Moisture Absorption
	Outstanding Surface Finish
	Ultra High Stiffness
Forms	Pellets
Generic	PARA
Processing Method	Injection Molding
RoHS Compliance	RoHS Compliant
Uses	Cell Phones
	Electrical/Electronic Applications
	Housings