- Nilit Nilamid A H2 FR HF2 Unfilled, Flame Retardant PA66/6 Co-Polymer
Nilit Nilamid A H2 FR HF2 Unfilled, Flame Retardant PA66/6 Co-Polymer
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, Unreinforced |
| Manufacturer | Nilit |
| Trade Name | Nilamid |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit Nilamid A H2 FR HF2 Unfilled, Flame Retardant PA66/6 Co-Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Nilamid A H2 FR HF2 is an unfilled, flame retardant NYLON 66/6 co-polymer that does not contain halogen or red phosphorous. This product combines excellent flow characteristics and extremely fast cycle times with outstanding elongation and impact strength and a good thermal performance. Because of its excellent processing characteristics it is often used in complicated components. Typical applications include Terminal blocks, electrical cooling fans and housings, fuse boxes and carriers and flame retardant cable ties. This product can be supplied in a full range of colors and has an excellent surface finish. Laser marking grades are available. Key characteristics: Easy processingFast cyclingGood heat aging characteristics: UL RTI listing (mechanical) up to 140°C V0 listing at 0.4 mmHalogen and red phosphorous freeExcellent CTI value (600 V)Good impact strengthGood elongation Information provided by NILIT.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 1.5 % | 1.5 % | 23°C, 24h in H<sub>2</sub>O; sim. ISO 62 |
| Water Absorption at Saturation | 7.5 % | 7.5 % | sim. ISO 62 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | Euronil |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | Euronil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527, ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | |
| Tensile Modulus | 3.60 GPa | 522 ksi | ISO 527, ASTM D638 |
| Flexural Yield Strength | 110 MPa | 16000 psi | ISO 178, ASTM D790 |
| 30.0 MPa @Temperature 90.0 °C |
4350 psi @Temperature 194 °F |
ISO 178, ASTM D790 | |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178, ASTM D790 |
| 0.850 GPa @Temperature 90.0 °C |
123 ksi @Temperature 194 °F |
ISO 178, ASTM D790 | |
| Izod Impact, Notched (ISO) | 2.50 kJ/m² @Temperature -30.0 °C |
1.19 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 3.50 kJ/m² @Temperature 23.0 °C |
1.67 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179 |
| 3.60 J/cm² @Temperature -30.0 °C |
17.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179 |
| 0.350 J/cm² @Temperature -30.0 °C |
1.67 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 120 °C | 248 °F | 20,000 hr; IEC 216 |
| Deflection Temperature at 0.46 MPa (66 psi) | 207 °C | 405 °F | ISO 75, ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75, ASTM D648 |
| Vicat Softening Point | 220 °C | 428 °F | 49 N; ISO 306, ASTM D1525 |
| 235 °C | 455 °F | 9.8 N; ISO 306, ASTM D1525 | |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
|
| V-0 @Thickness 0.400 mm |
V-0 @Thickness 0.0157 in |
||
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
||
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Oxygen Index | 28 % | 28 % | ASTM D2863 |
| Glow Wire Test | 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
Glow Wire Flammability Index; IEC 694-2-12 |
| 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
Glow Wire Flammability Index; IEC 694-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 18.0 kV/mm @Thickness 2.00 mm |
457 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Comparative Tracking Index | >= 600 V @Thickness 3.20 mm |
>= 600 V @Thickness 0.126 in |
Sol. A; IEC 112, UL 746A |
| >= 600 V @Thickness 3.20 mm |
>= 600 V @Thickness 0.126 in |
Sol. B; IEC 112, UL 746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Nozzle Temperature | 270 - 280 °C | 518 - 536 °F | |
| Zone 1 | 260 - 270 °C | 500 - 518 °F | hopper |
| Zone 2 | 260 - 275 °C | 500 - 527 °F | |
| Zone 3 | 270 - 280 °C | 518 - 536 °F | |
| Zone 4 | 270 - 280 °C | 518 - 536 °F | |
| Melt Temperature | 265 - 280 °C | 509 - 536 °F | Do not melt above 280°C |
| Mold Temperature | >= 80.0 °C | >= 176 °F | |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 70.0 - 100 MPa | 10200 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clamping Force | in tons, 0.7 times the projected surface area in cm2 | |
| Flammability Rating | SE | FMVSS No. 302, 355x100x1 mm |
| Heat Resistance - Ball Test | OK | at 125°C, IEC 309 |
| OK | at 165°C, IEC 309 | |
| Holding Pressure | 90 MPa | |
| Needle Test | OK | IEC 695-2-2, 1 or 2 mm |
Users viewing this material also viewed the following:
- Orion Engineered Carbons CORAX® N 347 ASTM Carbon Black
- Raschig Group PiMC 1253 Highly flame retardant
- DuPont Performance Polymers Zytel® 73G35HSL BK262 Nylon 6 (Unverified Data**)
- Lord Adhesives 7701 Ethyl Acetate Surface Conditioner
- Techmer ES Luriblend® TPX-PA6/6-98020 40% Mineral Filled
- Samsung Cheil Industries Starex® SG-301 Expandable Polystyrene (EPS) High Expansion
- Borealis BS2581 High Density Polyethylene for Blow Molding
- Total LLDPE LL 1820 H Linear Low Density Polyethylene - Blown Film
- 3M 31U72C (Clear) Polyethylene Protective UV Tape
- Unipetrol PE HD LITEN® VL 20 N HDPE
Copyright © lookpolymers.com All Rights Reserved