- Gromax BFG20-FN00N1 Nylon 6 20% Glass Filled (Dry)
Gromax BFG20-FN00N1 Nylon 6 20% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BFG20-FN00N1 Nylon 6 20% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ISO 1183 |
| Moisture Absorption | 1.10 % | 1.10 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Temperature 80.0 °C |
0.0040 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Temperature 80.0 °C |
0.0080 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 91 | 91 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 137 MPa | 19900 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 5.5 % | 5.5 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 6.90 GPa | 1000 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 210 MPa | 30500 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 6.77 GPa | 981 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.90 kJ/m² | 4.24 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 0.920 J/cm² @Temperature 23.0 °C |
4.38 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXD941A PC
- Techmer ES Plastiblend® TPX-HTN-000CB 15% Glass Filled
- SABIC Innovative Plastics NORYL PX1265 PPE+PS
- Suqian Unitechem UV-P
- Polyram PB302G50 Nylon 6, 50% Glass Fiber
- TIMET TIMETAL® 550 (Ti-4Al-4Mo-2Sn) Titanium Alloy Solution Treated and Aged
- A. Schulman POLYBATCH™ Yellow 2450E Concentrate Based In Polyethylene
- Fainplast Compounds PH 50/1 Flexible PVC, Transparent Extrusion
- Azoty Tarnow™ TARNOFORM 300 GF3 POM
- 3M 9471PC Adhesive Transfer Tapes with Adhesive 300
Copyright © lookpolymers.com All Rights Reserved