SABIC Innovative Plastics Valox® 310SE0 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 310SE0 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
VALOX 310SE0 is an unreinforced, flame retardant PBT injection moulding resin. Applications: electrical industry, bobbins, keyboard, switches and switch components and appliance housings.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0800 % | 0.0800 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.36 % | 0.36 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.011 - 0.018 cm/cm | 0.011 - 0.018 in/in | on Tensile Bar; SABIC Method |
| 0.0090 - 0.016 cm/cm @Thickness 0.750 - 2.30 mm |
0.0090 - 0.016 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method | |
| 0.015 - 0.023 cm/cm @Thickness 2.30 - 4.60 mm |
0.015 - 0.023 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method | |
| 0.015 - 0.023 cm/cm @Thickness 3.20 mm |
0.015 - 0.023 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.019 cm/cm | 0.0090 - 0.019 in/in | on Tensile Bar; SABIC Method |
| 0.010 - 0.017 cm/cm @Thickness 0.750 - 2.30 mm |
0.010 - 0.017 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method | |
| 0.016 - 0.024 cm/cm @Thickness 2.30 - 4.60 mm |
0.016 - 0.024 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method | |
| Melt Flow | 8.6 g/10 min @Load 2.16 kg, Temperature 250 °C |
8.6 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Melt Index of Compound | 8.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ISO 2039-2 |
| Hardness, H358/30 | 105 MPa | 15200 psi | ISO 2039-1 |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 20 % | 20 % | Type I, 50 mm/min; ASTM D638 |
| 20 % | 20 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| 20 % | 20 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.80 GPa | 406 ksi | 1 mm/min; ISO 527 |
| 2.82 GPa | 409 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| 101 MPa | 14600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.60 GPa | 377 ksi | 2 mm/min; ISO 178 |
| 2.62 GPa | 380 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| 0.220 J/cm @Temperature -30.0 °C |
0.412 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 16.02 J/cm | 30.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| 3.00 kJ/m² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/2C |
| 0.800 J/cm² | 3.81 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 200 J @Temperature 23.0 °C |
148 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Taber Abrasion, mg/1000 Cycles | 19 | 19 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 76.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| 100 µm/m-°C @Temperature 23.0 - 60.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.9 @Frequency 50.0 - 60.0 Hz |
2.9 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 15.0 kV/mm @Thickness 3.20 mm |
381 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 18.0 kV/mm @Thickness 1.00 mm |
457 kV/in @Thickness 0.0394 in |
short time; IEC 60243-1 | |
| 18.4 kV/mm @Thickness 3.20 mm |
467 kV/in @Thickness 0.126 in |
in air; ASTM D149 | |
| 22.0 kV/mm @Thickness 1.60 mm |
559 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | |
| 24.0 kV/mm @Thickness 1.60 mm |
610 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 31.0 kV/mm @Thickness 0.800 mm |
787 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0010 @Frequency 50.0 - 60.0 Hz |
0.0010 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.0020 @Frequency 100 Hz |
0.0020 @Frequency 100 Hz |
IEC 60250 | |
| 0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| 60 - 120 sec | 60 - 120 sec | UL 746A | |
| Comparative Tracking Index | >= 100 V | >= 100 V | IEC 60112 |
| 175 V | 175 V | IEC 60112 | |
| 175 - 250 V | 175 - 250 V | UL 746A | |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® TPE 1503 Conductive Thermoplastic Compound
- Polykemi AB POLYshine PBT D221 PBT, Impact Modified
- Lehmann & Voss LUVOCOM® 3/CF/10/BK Polyamide 6, with carbon fiber
- Garlock Bay State 22 Natural/SBR Sheet Rubber
- MetalTek MTEK 316L Cast UNS J92800 Austenitic Stainless Steel
- A. Schulman POLYBATCH™ Brown 1281 Concentrate Based In Polyethylene
- Hexcel® Redux® 610W (0.09 psf) Flame retarded epoxy film adhesive
- ExxonMobil LLDPE LL 1002YB Cast Linear Low Density Polyethylene Resin
- Dow Corning 346 EMULSION
- C.O.I.M. LARIPUR® LPR5760 PTMG Polyether Polyurethane
Copyright © lookpolymers.com All Rights Reserved