Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
DIN 53479
Qualchem Danamid FEW-25 Polyamide 6, 25% Mineral Filled
Filled with mineralsInformation provided by Qualchem Zrt.
Density 1.40 g/cc
0.0506 lb/in³
ASTM D792
Victrex® PEEK 450CA30 30% Carbon Fiber Reinforced
General purpose, 30% carbon fiber reinforced, pelletized grade for injection molding.Information provided by Victrex.
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Pasargad Polymer Peyvand Pasamid 3P-H1135B Nylon 6, 35% Glass Fiber Reinforced
Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Electrical PartsFastenerHousingInformation provided by Pasargad Polymer Peyvand Co
Density 1.40 - 1.40 g/cc

@Temperature 280 - 280 °C
0.0506 - 0.0506 lb/in³

@Temperature 536 - 536 °F
Average value: 1.40 g/cc Grade Count:1
Overview of materials for Nylon 66, 30% Mineral Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Mineral Filled". Specific grades with primary filler content between 25% and 34% are inclu..
Density 1.40 g/cc

@Temperature 23.0 °C
0.0506 lb/in³

@Temperature 73.4 °F
ASTM D1505-68, method C
Mitsubishi Hostaphan® RN, 350 micron Nominal Thickness Universal Polyethylene Terephthalate Film
Hostaphan® RN is a biaxially oriented film made of polyethylene terephthalate (PET) and characterized by outstanding physical properties.Applications:Films for industrial applicationsCoatingLamin..
Density 1.40 g/cc
0.0506 lb/in³
LATI Latamid 6 H2 G/30-V0HF1 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Very good electrical properties.Availability: Africa &..
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
SABIC Innovative Plastics LNP LUBRICOMP KI001XXJ Acetal
LNP* LUBRICOMP* KI001XXJ is a compound based on Acetal containing 2% Silicone. Added features of this grade include: Wear Resistant, Healthcare.
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
SABIC Innovative Plastics LNP LUBRICOMP RFL25ES PA 66 (Europe-Africa-Middle East)
LNP* Lubricomp* RFL25ES is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Easy Molding.
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
SABIC Innovative Plastics LNP LUBRILOY K2000 Acetal
LNP LUBRILOY* K2000 is a compound based on Acetal resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Density 1.40 g/cc
0.0506 lb/in³
ASTM D792
SABIC Innovative Plastics LNP THERMOCOMP RF006EXZ PA 66
LNP THERMOCOMP* RF006EXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Easy Molding.
Density 1.40 g/cc
0.0506 lb/in³
ASTM D 792
SABIC Innovative Plastics LNP Thermocomp YF005
LNP* Thermocomp* YF005 is a compound based on TPEE resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Density 1.40 g/cc
0.0506 lb/in³
ASTM D792
Plenco 7100 Phenolic, Nodular, Injection Molded
PLENCO 07100 is an organic fiber reinforced phenolic molding compound, with improved mechanical strength properties and an industrial finish. 07100 is densified for easy handling and good pourabilit..
Density 1.40 g/cc
0.0506 lb/in³
ASTM D792
Plenco 7321 Phenolic, Granular, Transfer Molded
PLENCO 07321 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength and excellent dimensional stability. Type ASTM 5948 CFI-5, and UL recognized under compon..
Density 1.40 g/cc
0.0506 lb/in³
DIN 53479
Polyram PlusTek PB300G7 Nylon 6, 35% Glass Fiber
35% glass-fiber reinforced, heat stabilized polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Density 1.40 g/cc
0.0506 lb/in³
Trelleborg Emerson & Cuming Eccobond® 26 Two-Component General Purpose Epoxy Adhesive
Emerson & Cuming 26 Eccobond® Two-Component General Purpose Epoxy AdhesiveFilled, room temperature curing, general purpose, epoxy adhesive. Recommended for varied uses including repair and manufact..
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
EMS-Grivory Grivory® HT2C-3X LF black 9833 PA6T/66-CF30
Product description: Grivory HT2C-3X LF black 9833 is a 30% carbon-fibre reinforced, PTFE modified engineering thermoplastic based on semicrystalline partially aromatic copolyamide. Polymer designat..
Density 1.40 g/cc
0.0506 lb/in³
Cloth 1.75 g/cc per He measurement
Cytec Thornel® VCL Carbon Cloth Laminate with Mil R-9299 Resin
Data provided by the manufacturer, Amoco Performance Products, Inc.Carbon and graphite cloths, consisting entirely of flexible filaments, are produced by pyrolysis of rayon cloth at high temperature..
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Eurostar Staramide RF007S PA66, 35% Glass Fiber Filled, Injection Molded
Staramide RF007S is a 35% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
Density 1.40 g/cc
0.0506 lb/in³
Average value for Mylar® films.
DuPont Teijin Films Mylar® LBT Polyester Film, 48 Gauge (12 µm)
Data provided by DuPont Packaging Polymers.An uncoated, transparent polyester film that has been corona-treated to provide superior wetting and adhesion to inks, primers, and adhesives. Standard th..
Density 1.40 g/cc
0.0506 lb/in³
Calculated from nominal thickness and yield
DuPont Teijin Films Mylar® OB12 Polyester Packaging Film, 100 Gauge
Data provided by DuPont Packaging Polymers.Mylar® OB12 is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and polyvinylidene chloride (PVDC) layer on the oppo..
Density 1.40 g/cc
0.0506 lb/in³
DuPont Teijin Films Mylar® OWF Polyester Film, 48 Gauge
Product Description: Mylar® OWF is a co-extruded, one side amorphous, heat sealable polyester film designed to be used as an overwrap film. This film is suitable for use in contact with food. Appro..
Density 1.40 g/cc
0.0507 lb/in³
ASTM D792
Ensinger Tecaform™ Acetal Copolymer - Extruded Products (POM)
Tecaform™ is a semi-crystalline thermoplastic offering high strength, stiffness and toughness. It is resistant to hot water, hydrocarbons and solvents, and it posses good bearing and wear properti..
Density 1.40 g/cc
0.0506 lb/in³
BASF LUMOGEN® 300 F Red
Type of Dye: PeryleneNote on Fastness to Weathering: 0.02% in PMMA injection-molded plaques of 2 mm thickness Residual fluorescence(%) after 80 days accelerated exposure in Xenotest 1200Information ..
Density 1.40 g/cc
0.0506 lb/in³
ASTM D792
Beijing Chemical Industry KAIFA® 301-G0F PBT Resin
Flame retardant, good flow, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group)
Density 1.40 g/cc
0.0506 lb/in³
ASTM D792
Ashley Polymers Ashlene® 63M Nylon 66, Mineral Filled
A mineral filled Nylon 66 providing superior stiffness and dimensional stability.Data provided by the manufacturer
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
BASF Ultramid® 1503-2F BK ND 3007 33% Glass Filled PA 66 (Dry)
Description: Ultramid 1503-2F BK ND3007 is a 33% glass reinforced, heat stabilized injection molding PA6/6 grade. It is designed to provide enhance hydroysis resistance for under-the-hood applicatio..
Density <= 1.40 g/cc
<= 0.0506 lb/in³
cured 14 days @ 50% RH
3M AC-350 Class B-1/4 Aerospace Sealant
3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are..
Density 1.40 g/cc
0.0506 lb/in³
Crystalline Density; ASTM D1505
Eastman 5214A PET  (discontinued **)
Voridian PET 5214A is a bright and transparent amber homopolymer that meets light barrier requirements while maintaining the desirable attributes of PET. This resin is commonly used to mold containe..