Multibase Multi-Pro® 3012 RC Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Multibase
Trade Name Multi-Pro®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase Multi-Pro® 3012 RC Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Glass Fiber Reinforced, 30% by weight.Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM D955
Melt Flow 7.0 g/10 min
7.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 83
83
ASTM D2240
Tensile Strength, Yield 40.5 MPa
5870 psi
ASTM D638
Elongation at Break 17 %
17 %
ASTM D638
Flexural Yield Strength 60.8 MPa
8820 psi
ASTM D790
Flexural Modulus 3.90 GPa
565 ksi
ASTM D790
Izod Impact, Notched 0.481 J/cm
0.900 ft-lb/in
73°F; ASTM D256
Gardner Impact 9.039 J
6.667 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 163 °C
325 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 143 °C
290 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 199 - 260 °C
390 - 500 °F
Middle Barrel Temperature 204 - 260 °C
400 - 500 °F
Front Barrel Temperature 216 - 260 °C
420 - 500 °F
Nozzle Temperature 216 - 249 °C
420 - 480 °F
Mold Temperature 4.44 - 65.6 °C
40.0 - 150 °F
Drying Temperature 93.3 °C
200 °F
Dry Time 2 hour
2 hour
Back Pressure 0.138 - 0.345 MPa
20.0 - 50.0 psi
Screw Speed 40 - 100 rpm
40 - 100 rpm