SABIC Innovative Plastics NORYL GTX GTX974 PPE+PA
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX974 PPE+PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NORYL GTX974 is a material especially designed for in- or on-line painted bodypanels and fenders in particular. This material combines impact performance with conductivity for electro-static painting in an unique way.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.20 % | 1.20 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 4.2 % | 4.2 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.013 - 0.016 cm/cm <br>@Thickness 3.20 mm |
0.013 - 0.016 in/in <br>@Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.011 - 0.014 cm/cm <br>@Thickness 3.20 mm |
0.011 - 0.014 in/in <br>@Thickness 0.126 in |
SABIC Method |
| Melt Flow | 10 g/10 min <br>@Load 5.00 kg,<br> Temperature 280 °C |
10 g/10 min <br>@Load 11.0 lb,<br> Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 12 g/10 min <br>@Load 5.00 kg,<br> Temperature 280 °C |
12 g/10 min <br>@Load 11.0 lb,<br> Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
| 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 30 % | 30 % | 50 mm/min; ISO 527 |
| 50 % | 50 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.00 GPa | 290 ksi | 1 mm/min; ISO 527 |
| 2.05 GPa | 297 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 75.0 MPa | 10900 psi | 2 mm/min; ISO 178 |
| 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
| 2.05 GPa | 297 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.80 J/cm | 3.37 ft-lb/in | ASTM D256 |
| 1.20 J/cm <br>@Temperature -30.0 °C |
2.25 ft-lb/in <br>@Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | 80*10*4; ISO 180/1A |
| 10.0 kJ/m² <br>@Temperature -30.0 °C |
4.76 ft-lb/in² <br>@Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.00 J/cm² <br>@Temperature -30.0 °C |
4.76 ft-lb/in² <br>@Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 50.0 J <br>@Temperature 23.0 °C |
36.9 ft-lb <br>@Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C <br>@Temperature -40.0 - 40.0 °C |
50.0 µin/in-°F <br>@Temperature -40.0 - 104 °F |
ASTM E 831 |
| 100 µm/m-°C <br>@Temperature 23.0 - 60.0 °C |
55.6 µin/in-°F <br>@Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C <br>@Temperature 23.0 - 60.0 °C |
50.0 µin/in-°F <br>@Temperature 73.4 - 140 °F |
ISO 11359-2 |
| 100 µm/m-°C <br>@Temperature -40.0 - 40.0 °C |
55.6 µin/in-°F <br>@Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 180 °C <br>@Thickness 3.20 mm |
356 °F <br>@Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 175 °C | 347 °F | Rate B/50; ISO 306 |
| 180 °C | 356 °F | Rate B/120; ISO 306 | |
| 180 °C | 356 °F | Rate B/50; ASTM D1525 | |
| 230 °C | 446 °F | Rate A/50; ISO 306 | |
| Flammability, UL94 | HB <br>@Thickness 1.50 mm |
HB <br>@Thickness 0.0591 in |
UL 94 |
| HB <br>@Thickness 3.00 mm |
HB <br>@Thickness 0.118 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 - 10000 ohm-cm | 1000 - 10000 ohm-cm | SABIC Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Polimeri Europa Clearflex® CH D0 Very Low Density Polyethylene
- Inno-Comp INNOPOL® CS 1-3130 30% Talc-Filled Polypropylene Homopolymer
- Shandong Dongyue Shenzhou New Material Co Perfluoro-3,6-dioxa-4-methyl-7-octene-sulfonylfluoride (PSVE)
- Teknor Apex Telcar® TL-1120E Thermoplastic Elastomer
- A. Schulman POLYBATCH™ Silver 70100 Concentrate Based In LDPE
- DuPont Performance Polymers Zytel® FE270050 BK099 Nylon 66 (Unverified Data**)
- Clariant Renol 6608G33HSL Nylon 66, 33% Glass Fiber, Impact Modified, Heat Stabilized, Lubricated
- Asahi Glass Lumiflon LF-200 Solvent Soluble Fluoropolymer w/ isocyanate hardening agent
- Beijing Ranger Chem SM-602RX75 Solvent Based Epoxy Resin
- Bhansali Engineering Abstron HCR-15 M ABS Heat Resistant
Copyright © lookpolymers.com All Rights Reserved