SABIC Innovative Plastics NORYL CTI2550 PPE+HIPS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL CTI2550 PPE+HIPS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NORYL CTI2550 is a glass/mineral filled material with a Vicat B/120 of 160 °C according ISO 306.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ISO 1183
Moisture Absorption 0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.25 %
0.25 %
ISO 62
Linear Mold Shrinkage, Flow 0.0030 - 0.0040 cm/cm
0.0030 - 0.0040 in/in
on Tensile Bar; SABIC Method
Melt Index of Compound 19 g/10 min

@Load 10.0 kg,
Temperature 280 °C
 19 g/10 min

@Load 22.0 lb,
Temperature 536 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 115 MPa
16700 psi
ISO 2039-1
Tensile Strength at Break 75.0 MPa
10900 psi
5 mm/min; ISO 527
Elongation at Break 1.2 %
1.2 %
5 mm/min; ISO 527
Tensile Modulus 8.00 GPa
1160 ksi
1 mm/min; ISO 527
Flexural Strength 105 MPa
15200 psi
2 mm/min; ISO 178
Flexural Modulus 7.00 GPa
1020 ksi
2 mm/min; ISO 178
Izod Impact, Unnotched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
80*10*4; ISO 180/1U
13.0 kJ/m²

@Temperature -30.0 °C
 6.19 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 1.50 J/cm²
7.14 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
1.40 J/cm²

@Temperature -30.0 °C
 6.66 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
1.50 J/cm²

@Temperature -30.0 °C
 7.14 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
Taber Abrasion, mg/1000 Cycles 60
60
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 13.9 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 45.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 25.0 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Thermal Conductivity 0.260 W/m-K
1.80 BTU-in/hr-ft²-°F
ISO 8302
Hot Ball Pressure Test <= 145 °C
<= 293 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 140 °C
284 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 155 °C
311 °F
Rate B/50; ISO 306
160 °C
320 °F
Rate B/120; ISO 306
165 °C
329 °F
Rate A/50; ISO 306
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 V-1

@Thickness 1.50 mm
 V-1

@Thickness 0.0591 in
 UL 94
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 UL 94
Oxygen Index 35 %
35 %
ISO 4589
Glow Wire Test 960 °C

@Thickness 2.50 mm
 1760 °F

@Thickness 0.0984 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
 2.9

@Frequency 1.00e+6 Hz
 IEC 60250
2.9

@Frequency 50.0 - 60.0 Hz
 2.9

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 18.0 kV/mm

@Thickness 3.20 mm
 457 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
Dissipation Factor 0.0040

@Frequency 50.0 - 60.0 Hz
 0.0040

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.0040

@Frequency 1.00e+6 Hz
 0.0040

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 250 V
250 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2