LyondellBasell Petrothene® NA362005 Low Density Polyethylene

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer LyondellBasell (former Equistar)
Trade Name Petrothene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LyondellBasell Petrothene® NA362005 Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ApplicationsPETROTHENE NA 362 is a series of low density/EVA copolymers designed for ice bags, bag-in-box, heavy-duty skin packaging and other high strength, easy to seal packaging. NA 362 exhibits high impact strength and good low temperature toughness. Regulatory StatusThe base resin NA 362 meets the requirements of the Food and Drug Administration regulation 21 CFR 177.1350. This regulation allows the use of this ethylene vinyl acetate copolymer "…in articles or components of articles intended for use in contact with food." Specific limitations or conditions of use may apply. Contact your Equistar sales representative for more information. Processing TechniquesSpecific recommendations for processing NA 362 can only be made when the processing conditions, equipment and end use are known. For further suggestions, contact your Equistar sales representative.Physical PropertiesThese are typical values and not to be construed as specific product limits. Data obtained from film produced in a 3.5"(89mm) blown film line, commercially available 8"(203 mm)die, 430°F(221°C) melt extrusion temperature, 2:1 BUR, 2.0 mil (51 micron) gauge, 0.025" die gap at 170 lb/hr.This product is from the former Equistar product line.
Physical Properties Metric English Comments
Density 0.926 g/cc
0.0335 lb/in³
ASTM D1505
Vinyl Acetate Content 6.6 %
6.6 %
Thickness 50.8 microns
2.00 mil
2:1 BUR; 25 mil die gap
Melt Flow 0.50 g/10 min
0.50 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 500 %
500 %
ASTM D882
Film Elongation at Break, TD 600 %
600 %
ASTM D882
Elmendorf Tear Strength MD 140 g
140 g
ASTM D1922
Elmendorf Tear Strength TD 260 g
260 g
ASTM D1922
Dart Drop Test 310 g
0.684 lb
F<sub>50</sub>; ASTM D1709
Film Tensile Strength at Break, MD 26.2 MPa
3800 psi
ASTM D882
Film Tensile Strength at Break, TD 24.8 MPa
3600 psi
ASTM D882
1% Secant Modulus, MD 117 MPa
17000 psi
ASTM D882
1% Secant Modulus, TD 145 MPa
21000 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 87.0 °C
189 °F
ASTM D1525
Processing Properties Metric English Comments
Melt Temperature 221 °C
430 °F
Descriptive Properties Value Comments
Antiblock None
Slip None