Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527-2/1 |
PolyOne Trilliant™ HC HC6200-5001 XR Grey Polyamide 12 (Nylon 12) The Trilliant® specialty compounds offer a complete system of specialty engineered materials, certified processes, services and technical support that enable healthcare OEM's to get to market ahead.. |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | 50 mm/min; ASTM D638 |
Ovation Polymers RIGITRON 20443 GF PBT, 43% Glass Reinforced PBT - Glass reinforced (43 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared acco.. |
|||
Tensile Modulus | 8.00 GPa @Thickness 0.0178 mm |
1160 ksi @Thickness 0.000701 in |
ASTM D882-02 |
NeXolve Novastrat® 800 Polyimide High temperature polyimide film with low coefficient of thermal expansion.NeXolve Novastrat® 800 is a high temperature polyimide film with low coefficient of thermal expansion (CTE), ~4 ppm/°C fro.. |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | |
Radici Radiflam® A RV300AF (cond.) Nylon 66-30GF Radiflam® A is a range of flame retardant polyamides 66 (PA 66) used for injection molding and extrusion for all applications where high fire resistance is required.Information provided by Radici g.. |
|||
Tensile Modulus | 8.00 GPa @Temperature 150 °C |
1160 ksi @Temperature 302 °F |
ISO 527-2 |
Solvay Specialty Polymers Amodel® A-1145 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel A-1145 HS is a 45% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, very high flexural modulus and very high tensile strength. Excellent creep .. |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527, ASTM D638 |
Nilit Nilamid A G5 FR C4 25% Glass Fiber Reinforced, Flame Retardant PA66 (with Halogens) Description: Nilamid A G5 FR C4 combines excellent mechanical performance with flame retardancy. The halogenated flame retardant system used in this product allows a wide range of colors. This produ.. |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527, ASTM D638 |
Nilit Nilamid B G6 FR C4 30% Glass Fiber Reinforced, Flame Retardant PA6 Description: Nilamid B G6 FR C4 combines excellent mechanical performance with flame retardancy. The halogenated flame retardant system used in this product allows a wide range of colors. This produ.. |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527 |
Nilit FRIANYL B63 H-GV25 Nylon 6 for injection molding, 25% glass fiber reinforced Nylon 6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527 |
Nilit FRIANYL B63 W-GV25 Nylon 6 for injection molding, 25% glass fiber reinforced Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DCL32 PC (Europe-Africa-Middle East) LNP* LUBRICOMP* DCL32 is a compound based on Polycarbonate resin contqaining Carbon Fiber, PTFE. Added features include; Internally Lubricated, Electrically Conductive. |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527-1/-2 |
DSM Akulon® K224-HG5 Nylon 6-25% Glass Reinforced (European and Asian Grade) (Dry)
(discontinued **) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527 Type 1A |
Solvay TECHNYL® A 60 G1 V25 PA66, 25% glass fiber, Conditioned Description: TECHNYL® A 60G1 V25 is a 25% GF reinforced organophosphorous flame retarded grade based on a patented high flow polyamide 66 resin. This product is heat stabilized and provides optim.. |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | DIN 53457 |
Schwartz Technical Plastics MITELA® HD8B Cotton Fabric, Special Quality Application: bearing shells and bearing collarsInformation provided by Schwartz Technical Plastics GmbH |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 830F PBT+PET PBT+PET, 30% Glass, Mold Release, Heat Stabilized, For food contact applications |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL GFN3 PPE+HIPS (Europe-Africa-Middle East) Noryl GFN3 is a standard 30 % glass filled material with a HDT/A of 145C according to ISO 75 |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | 1 mm/min; ISO 527-1 |
Sax Polymers SAXAMID 126F5 Nylon 6, 25% Glass Fiber SAXAMID 126F5 is a polyamide 6 injection-molding-grade reinforced with 25% glass fibers.Information provided by SAX Polymers |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | ASTM D638 |
Plenco 7507 Phenolic, Granular, Transfer Molded PLENCO 07507 is an organic reinforced phenolic molding compound offering improved dimensional stability under humid conditions. 07507 offers excellent resistance to degradation from detergent solut.. |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527 |
Polyram PlusTek PA4802G6BK10 Nylon 66 for Injection Molding, 30% Glass Fiber Reinforced, PTFE Lubricated 30% Glass fiber reinforced, PTFE lubricated Nylon 66 for injection molding application.Information provided by Polyram. |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | cond; ISO 527-1/-2 |
DSM Stanyl® OCD2300 BLK PA46-GF50 50% Glass Reinforced, Heat Stabilized |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527-1/-2 |
DSM Stanyl® TE250F3 (DAM) Nylon 46 15% Glass Reinforced, Heat Stabilized, Flame Retardant (North America) Information provided by DSM Engineering Plastics. |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527-1/-2 |
DSM Stanyl® TE250F6 (COND) Nylon 46 30% Glass Reinforced, Heat Stabilized, Flame Retardant (North America) Information provided by DSM Engineering Plastics. |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527-1/-2 |
DSM Stanyl® TW200F8 (COND) Nylon 46 40% Glass Reinforced, Heat Stabilized (North America) Information provided by DSM Engineering Plastics. |
|||
Tensile Modulus | 8.00 GPa @Temperature 120 °C |
1160 ksi @Temperature 248 °F |
ISO 527-1/-2 |
DSM Stanyl® TW341-J PA46 Heat Stabilized, Lubricated |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | 1 mm/min; ISO 527 |
Eurostar Staramide BG6 PA6, 30% Glass Filled, Injection Molded BG6 is a 30% Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier. |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527 |
Eurotec® Tecomid® NB40 GR20 NL XA70 PA6, 20% glass fiber reinforced, flame retardant - halogen (RoHS compliant), heat stabilized, natural Information provided by Eurotec® |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | 1 mm/min |
Arkema Group Rilsan® AZM 30 NOIR T6LD Nylon 12, 30% Glass Fiber Filled (Dry) Designation ISO 1874-PA12,MHLR,16-060,GF30Rigid grade with glass fiber (30%) for injection molding. Available color: black. Reinforced light and heat stabilizing agent. Mold-release agent.High rigid.. |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | dry; ISO 527 |
Azoty Tarnow™ Tarnamid® T-27 GF25 Polyamide 6 - Glass Fiber Reinforced 25% Glass fiber reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High.. |
|||
Tensile Modulus | 8.00 GPa @Temperature 70.0 °C, Time 720000 sec |
1160 ksi @Temperature 158 °F, Time 200 hour |
62% RH |
Akro-Plastic Akromid® B3 GF 30 9 RM-M (3099) PA 6 Dry, 30% Glass Filled In all, the construction relevant features show that the significantly reduced moisture absorption of AKROMID B3 GF 30 RM leads to increasing rigidities and strengths as already expected. Neverthele.. |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527-2 |
Pasargad Polymer Peyvand Pasamid 3P-M1130B Nylon 6, 30% Glass Fiber Reinforced Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Electrical PartsFastenerHousingInformation provided by Pasargad Polymer Peyvand Co |
|||
Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527-2 |
Ascend Performance Materials Vydyne® R633 Nylon 66 Copolymer, 33% Glass Filled, Conditioned (2.5% Moisture) Vydyne® R633 is 33% glass-fiber reinforced, PA66/6 copolymer resin for superior surface appearance. Available in natural, this injection-molding grade resin is lubricated for machine feed and mold .. |