Category | Polymer , Thermoplastic , Polycarbonate (PC) |
Manufacturer | SABIC Innovative Plastics (GE Plastics) |
Trade Name | Lexan® |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | SABIC Innovative Plastics Lexan® LUX2614G PC (Europe-Africa-Middle East).pdf |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
Water Absorption | 0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
ASTM D570 |
Moisture Absorption at Equilibrium | 0.35 % | 0.35 % | ASTM D570 |
0.58 % @Temperature 100 °C |
0.58 % @Temperature 212 °F |
ASTM D570 | |
Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
Melt Flow | 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Melt Index of Compound | 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Rockwell M | 70 | 70 | ASTM D785 |
Hardness, Rockwell R | 118 | 118 | ASTM D785 |
Tensile Strength at Break | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D638 | |
Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 |
63.0 MPa | 9140 psi | 50 mm/min; ISO 527 | |
Elongation at Break | 110 % | 110 % | Type I, 50 mm/min; ASTM D638 |
Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D638 | |
Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 |
Flexural Yield Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
94.0 MPa | 13600 psi | 2 mm/min; ISO 178 | |
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
Izod Impact, Notched | 7.50 J/cm | 14.1 ft-lb/in | ASTM D256 |
Izod Impact, Unnotched | 32.0 J/cm | 59.9 ft-lb/in | ASTM D4812 |
Tensile Impact Strength | 546 kJ/m² | 260 ft-lb/in² | Type S; ASTM D1822 |
Dart Drop, Total Energy | 169 J | 125 ft-lb | ASTM D3029 |
Taber Abrasion, mg/1000 Cycles | 10 | 10 | CS-17, 1 kg; ASTM D1044 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 68.4 µm/m-°C @Temperature -40.0 - 95.0 °C |
38.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
Specific Heat Capacity | 1.26 J/g-°C | 0.301 BTU/lb-°F | ASTM C351 |
Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | ASTM C177 |
Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 132 °C @Thickness 6.40 mm |
270 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Vicat Softening Point | 145 °C | 293 °F | Rate B/120; ISO 306 |
154 °C | 309 °F | Rate B/50; ASTM D1525 | |
UL RTI, Electrical | 130 °C | 266 °F | UL 746B |
UL RTI, Mechanical with Impact | 125 °C | 257 °F | UL 746B |
UL RTI, Mechanical without Impact | 125 °C | 257 °F | UL 746B |
Flammability, UL94 | V-2 @Thickness 0.750 - 3.00 mm |
V-2 @Thickness 0.0295 - 0.118 in |
UL 94 |
Glow Wire Test | 850 °C | 1560 °F | IEC 60695-2-13 |
875 °C | 1610 °F | IEC 60695-2-13 | |
750 °C @Thickness 0.750 mm |
1380 °F @Thickness 0.0295 in |
IEC 60695-2-12 | |
850 °C @Thickness 1.50 mm |
1560 °F @Thickness 0.0591 in |
IEC 60695-2-12 |
Optical Properties | Metric | English | Comments |
---|---|---|---|
Refractive Index | 1.586 | 1.586 | ASTM D542 |
Haze | 1.0 % @Thickness 2.54 mm |
1.0 % @Thickness 0.100 in |
ASTM D1003 |
Transmission, Visible | 88 % | 88 % | 2.54 mm; ASTM D1003 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | ASTM D257 |
Dielectric Constant | 2.96 @Frequency 1.00e+6 Hz |
2.96 @Frequency 1.00e+6 Hz |
ASTM D150 |
3.17 @Frequency 50.0 - 60.0 Hz |
3.17 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
Dielectric Strength | 15.0 kV/mm @Thickness 3.20 mm |
381 kV/in @Thickness 0.126 in |
in air; ASTM D149 |
Dissipation Factor | 0.00090 @Frequency 50.0 - 60.0 Hz |
0.00090 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
ASTM D150 | |
Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | UL 746A |
High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A |
Descriptive Properties | Value | Comments |
---|---|---|
Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Specific Volume | 0.83cm^3/g | ASTM D792 |
UV-light, water exposure/immersion | F2 | UL 746C |