PolyOne Maxxam™ SY 89-22-7 Polypropylene, Unspecified (PP, Unspecified)

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	PolyOne Corporation
Trade Name	Maxxam™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Maxxam™ SY 89-22-7 Polypropylene, Unspecified (PP, Unspecified).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Maxxam ™ SY 89-22-7 is a polypropylene copolymer compound with a pre-dispersed blowing agent for up to 60% expansion. The compound offers consistent cell structure, dielectric properties, and strength on insulation walls as thin as 10 mils.NOTE: 1. Typical properties of molded slab (0.075); Not to be construedas specifications.2. Foam density reduction depends upon loading level, temperatureand residence time before cooling.3. Recommended process temperature: 190°C to 220°C (375°F to430°F).Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	0.519 g/cc	0.519 g/cc	ASTM D792
Melt Flow	2.1 g/10 min @Load 2.16 kg, Temperature 190 °C	2.1 g/10 min @Load 4.76 lb, Temperature 374 °F	Procedure A; ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	23.4 MPa	3390 psi	Type IV, 510 mm/min; ASTM D638
Elongation at Break	400 %	400 %	Type IV, 510 mm/min; ASTM D638

Electrical Properties	Metric	English	Comments
Dielectric Constant	2.24 @Frequency 1000 Hz	2.24 @Frequency 1000 Hz	ASTM D150
Dissipation Factor	0.00030 @Frequency 1000 Hz	0.00030 @Frequency 1000 Hz	ASTM D150

Descriptive Properties	Value	Comments
Features	Foamable
Forms	Pellets
Generic Material	PP, Unspecified
Generic Name	Polypropylene, Unspecified (PP, Unspecified)
Processing Method	Extrusion
	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Cable Jacketing
	Communication Wire Insulation
	Wire & Cable Applications