Polymer Property : Melt Flow = 7.0 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 230 °C	7.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
RheTech Products F56-01 40% Glass Fiber/Mineral Co-Reinforced Polypropylene, Chemically Coupled, Black Applications: Consumer goodsUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 190 °C	7.0 g/10 min @Load 4.76 lb, Temperature 374 °F	Procedure A; ASTM D1238
PolyOne Maxxam™ FR MF5420-0085 NHFR Polypropylene, Unspecified (PP, Unspecified) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V..
Melt Flow	7.0 g/10 min @Load 3.80 kg, Temperature 230 °C	7.0 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D 1238
SABIC Innovative Plastics Cycoloy® C1950 PC+ABS Low viscosity injection molding resin.This data was supplied by SABIC-IP for the Americas region.
Melt Flow	7.0 g/10 min @Load 21.6 kg, Temperature 190 °C	7.0 g/10 min @Load 47.6 lb, Temperature 374 °F	Procedure A; ASTM D1238
PolyOne Maxxam™ DP 9052-3-1000 Polyethylene, High Density (HDPE) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 230 °C	7.0 g/10 min @Load 4.76 lb, Temperature 446 °F	STN EN ISO 1133
Plastcom SLOVAMID 6 HI-M PA6 with improved impact strength PA 6 with the content of thermoplastic elastomer. Impacted, for moldings with higher toughness even at low temperatures, suitable for external use, eg. ski shoes, sports and safety helmets, protecti..
Melt Flow	7.0 g/10 min @Load 5.00 kg, Temperature 200 °C	7.0 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D-1238
Chevron Phillips MA5350 HIPS - High Impact Polystyrene (discontinued **) Rubber modified high impact polystyrene.Applications:Floppy diskettesDurable household applicationsThin to medium parts that require a combination of high gloss and good toughnessFeatures:Low coeffi..
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 190 °C	7.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
DuPont Performance Polymers Delrin® 327UVE NC010 Acetal Homopolymer (Unverified Data**) Delrin® 327UVE NC010 (formerly DE20554) is a medium-high viscosity acetal homopolymer with UV stabilizers having extremely low VOC emissions, developed for automotive interior applications.Informat..
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 340 Â°C	7.0 g/10 min @Load 4.76 lb, Temperature 644 Â°F
Lehmann & Voss LUVOCOMÂ® 20-7847 Polyphthalamide, with carbon fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Low influence from moisture an..
Melt Flow	7.0 g/10 min	7.0 g/10 min	ASTM D1238
Hyosung Topilene C600Y PP C600Y Butene Random CopolymerApplications: FilmCharacteristics:Excellent transparency & glossLow sealing temperatureHigh hot-tack strengthGood stiffnessInformation provided by Hyosung Corporation
Melt Flow	7.0 - 10 g/10 min	7.0 - 10 g/10 min	ASTM D1238
Kolon KOCETALÂ® LF302 Wear Modified Acetal Resin Improved wear property and dimensional stability. Applications: Products for low noise and precision gear. Information provided by API-Kolon.
Melt Flow	7.0 g/10 min @Load 10.0 kg, Temperature 220 Â°C	7.0 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ASTM D1238
Kostat 7440 Conductive ABS Compound KOSTAT 7440 is a conductive thermoplastic compound based on Acrylonitrile Butadiene Styrene and a special carbon black. KOSTAT 7440 is not dependant on atmospheric conditions and is used for ESD in..
Melt Flow	7.0 g/10 min @Load 1.20 kg, Temperature 300 Â°C	7.0 g/10 min @Load 2.65 lb, Temperature 572 Â°F	ASTM D1238
LTL Color Compounds ColorFastÂ® PCGF120 Polycarbonate, 20% Glass-Filled 20% glass-filled grade, good balance of impact and mechanical propertiesAll information provided by LTL Color Compounders, Inc.
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 190 Â°C	7.0 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ISO 1133
Lucobit LucofinÂ® 1400MN Powder Ethylene Butyl Acrylate Lucofin 1400MN Powder is a polar copolymer consisting of ethylene and butyl acrylate with low crystallinity. Due to its chemical structure Lucofin 1400MN Powder is softer and more flexible ethane et..
Melt Flow	7.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 Â°C	7.0 - 12 g/10 min @Load 2.65 lb, Temperature 572 Â°F	ASTM D1238
Iran Petrochemical (PCC) PC 0712 Polycarbonate Suitable for molding and extrusionInformation provided by Iran Petrochemical Commercial Co.
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 343 Â°C	7.0 g/10 min @Load 4.76 lb, Temperature 649 Â°F	ASTM D1238
Solvay Specialty Polymers UdelÂ® P-1710 Polysulfone (PSU) UdelÂ® P-1710 polysulfone (PSU) is a tough, rigid, high-strength thermoplastic that is suitable for continuous use up to 300Â°F (149Â°C). The resin is resistant to oxidation and hydrolysis and..
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 190 Â°C	7.0 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238
Techmer ES HiFillÂ® POM CO 0241 S Acetal Availability: North AmericaForms: PelletsFiller/Reinforcement: MetalFeatures: CopolymerInformation provided by TP Composites, Inc.
Melt Flow	7.0 g/10 min @Load 1.20 kg, Temperature 300 Â°C	7.0 g/10 min @Load 2.65 lb, Temperature 572 Â°F	ASTM D1238
Styron EMERGEâ„¢ 4800-7 Polycarbonate EMERGEâ„¢ 4800-7 advanced resin provides superior ignition resistance in opaque, injection molding applications. Physical properties and process-ability are outstanding for this class of polycar..
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 230 °C	7.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Borealis Borsoft™ SD233CF High Impact Polypropylene Random Heterophasic Copolymer for Cast Film Borsoft SD233CF is a very soft random heterophasic copolymer, suitable for use on chill roll process. The product combines unique softness with outstanding mechanical properties making it the ideal..
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 190 °C	7.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
A. Schulman POLYBATCH™ White 8000 AP Concentrate Based In LDPE DescriptionPOLYBATCH® 8000 AP is an advanced performance white color concentrate containing 70% TiO2 based in LDPE. This product has been specifically engineered to provide improved resistance to ..
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 230 °C	7.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Polyram Metal Cap PPC371B73 Heavy Density Polypropylene, 73% Mineral Filled 73% Mineral filled, heavy density polypropylene copolymer for injection molding metalized part and galvanized covers.Information provided by Polyram.
Melt Flow	7.0 g/10 min @Load 1.20 kg, Temperature 300 °C	7.0 g/10 min @Load 2.65 lb, Temperature 572 °F	estimated from MVR using room temperature density; ISO 1133
Covestro Makrolon® DP1-1821* Polycarbonate Developmental productMVR (300 °C/1.2 kg) 6.0 cm3/10 minHigh viscosityUV stabilizedEasy releaseInjection moldingAvailable in colorless transparent onlyPreprocessingMax. Water content
Melt Flow	7.0 g/10 min @Load 10.0 kg, Temperature 220 °C	7.0 g/10 min @Load 22.0 lb, Temperature 428 °F	ASTM D1238
Diamond Polymers Centrex® 485 Sheet Extrusion Grade Centrex 485 resin is a low-gloss, medium-impact grade of ASA (acrylonitrile-styrene-acrylate) with good resistance to weather aging. It has good melt strength for extrusion and thermoforming, and it..
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 190 °C	7.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Barlog Plastics KEBAFORM C 901 CB POM Copolymer unreinforced, electr. conductive POMInformation provided by BARLOG plastics GmbH.
Melt Flow	7.0 g/10 min	7.0 g/10 min	ASTM D1238
Aclo Accutech Polyethylene HD0204UVL High Density UV Stabilized
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 230 °C	7.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
LyondellBasell Hifax™ CA186 Thermoplastic Olefin Resin Key Features: medium melt flow, medium modulus, paintable thermoplastic elastomeric olefin resin, excellent impact and stiffness balance, excellent paintability and paint durability, good processabi..
Melt Flow	7.0 g/10 min @Load 1.20 kg, Temperature 300 °C	7.0 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
SABIC Innovative Plastics Lexan® 950 PC (Asia Pacific) Opaque colors, high viscosity, superior flame retardance.
Melt Flow	7.0 g/10 min	7.0 g/10 min	±15%
Kazanorgsintez 11503-070 High Pressure Polyethylene Production Method: HDPE is produced by high pressure ethylene polymerization in tubular reactors. Application: Intended for production of bags, pipes, fittings, articles designed for food contac..