Polymer Property : Melt Index of Compound = 7.0 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most.
Physical Properties Metric English Comments
Melt Index of Compound 7.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 7.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Polykemi AB POLYelast TPE EDS80 D35 Thermoplastic Elastomer
Information provided by Polykemi AB
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 7.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® 104 PC
UL rated HB. 200 series recommended when V-2 rating required. 7.0 MFR, for thicker sections without sinks. FDA food contact compliant in limited colors.Effective January 15th, 2007 this grade will..
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 7.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® 500ECR PC
Lexan* 500ECR Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. It is of non-chlorinated & non-brominated flame retardant systems with UL-94 V0 rating at 2.3mm. It is a..
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 7.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® 500ECR PC (Europe-Africa-Middle East)
Lexan* 500ECR Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. It is of non-chlorinated & non-brominated flame retardant systems with UL-94 V0 rating at 2.3mm. It is a..
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 7.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® 505R PC
Lexan* 505R Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. Lexan 505R contains non-chlorinated, non-brominated flame retardant systems with UL-94 V0 rating at 1.5mm...
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 7.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® 505R PC (Europe-Africa-Middle East)
Lexan* 505R Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. Lexan 505R contains non-chlorinated, non-brominated flame retardant systems with UL-94 V0 rating at 1.5mm...
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 7.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® 505RU PC
Lexan* 505RU is a glass reinforced,flame retardant(FR)grade with non brominated and non chlorinated FR systems and UV stablization packages. This product is intended for applications to meet WEEE/Ro..
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 7.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® EXL6414 PC
PC-Siloxane copolymer with excellent processability. Impact modified, medium flow, extreme low temp. ductility.
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 7.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® LUX2614G PC (Asia Pacific)
Lexan LUX2614G (EXRL0944) is a diffusive, high viscosity, uv stabilized, flame retardant polycarbonate with improved light transmission and providing good colorstability under heat exposure. Develop..
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 7.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® LUX9612G PC (Europe-Africa-Middle East)
Lexan LUX9612G (EXRL0945) is a UV stabilized high viscosity, flame retardant polycarbonate featuring non brominated and non chlorinated FR system with diffusion effect and thin wall FR performance p..
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 7.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® EXL9330S PC Copolymer
Opaque PC-Siloxane copolymer with excellent processability. UV stabilized. UL rated V-0/5VA/CTI-PLC-2. Available in limited colors.
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 7.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® HP6NR PC
Low/med flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains no ..
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 250 °C
 7.0 g/10 min

@Load 2.65 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics PC4800 PC (Asia Pacific)
PC4800 resin is a very high flow (MFR = 8.0 at 250C/1.2kg) polycarbonate product designed for use in the optical media market.
Melt Index of Compound 7.0 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 7.0 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Valox® IQ357 PBT+PC (Asia Pacific)
Valox* Resin IQ357: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified.
Melt Index of Compound 7.0 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 7.0 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Valox® IQ357U PBT+PC
Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin.
Melt Index of Compound 7.0 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 7.0 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Xenoy® X4870HH PC+PET (Asia Pacific)
Xenoy X4870HH is a high heat, very high modulus and ductile PC/PET blend. Furthermore this resin provides chemical resistance, very low creep, low CTE, excellent fatique and high heat dimensional st..
Melt Index of Compound 7.0 g/10 min
7.0 g/10 min
Sibur ABS-C Molding Grade ABS Plastic
With high resistance to burning for bodies of devices, technical articles and consumer goods, and contacting with good products.
Melt Index of Compound 7.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 7.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics NORYL GTX GTX987 PPE+PA66
Conductive GTX, CTE 7
Melt Index of Compound 7.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 7.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics NORYL FXN121BK PPE+HIPS (Asia Pacific)
Noryl* FXN121BK is an unfilled modified polyphenylene ether resin suitable for injection molding. Designed to possess a unique low gloss surface appearance even when molded in polished tools, this r..
Melt Index of Compound 7.0 g/10 min

@Load 5.00 kg,
Temperature 300 °C
 7.0 g/10 min

@Load 11.0 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics NORYL GTX GTX678 PPE+PA (Europe-Africa-Middle East)
Noryl GTX678 resin is a high performance blend of PPE/PA that exhibits an excellent balance on non-halogenated flame retardance, conductivity, ductility, and high-heat resistance. This grade can be..
Melt Index of Compound 7.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 7.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 Condition E; ASTM D1238
A. Schulman LP390-01 Narrow Molecular Weight Copolymer
DescriptionLP 390-01 natural is a narrow molecular weight copolymer, high density polyethylene combining excellent impact strength with good environmental stress crack resistance.ApplicationLP 390-0..
Melt Index of Compound 7.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 7.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 Condition E; ASTM D1238
A. Schulman LP390-01 Narrow Molecular Weight Copolymer
DescriptionLP 390-01 natural is a narrow molecular weight copolymer, high density polyethylene combining excellent impact strength with good environmental stress crack resistance.ApplicationLP 390-0..
Melt Index of Compound 7.0 g/10 min

@Load 21.6 kg,
Temperature 150 °C
 7.0 g/10 min

@Load 47.6 lb,
Temperature 302 °F
 Fainplast
Fainplast Compounds HAX HF 22G Halogen Free PVC
Sheathing; standard grade improved processing speed
Melt Index of Compound 7.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 7.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Arkema Group OREVAC® 18921A Epoxide Modified Polyethylene
OREVAC® 18921A is epoxide modified polyethylene. It is available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyethylene (PE) resins. OREVAC® 18..
Melt Index of Compound 7.0 - 9.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 7.0 - 9.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ASTM D1238
Arkema Group LOTADER® 4603 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride
LOTADER 4603 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized by high pressure process in autoclave reactor. LOTADER 4603 is a multipurpose extrusion adhesive used..
Melt Index of Compound 7.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 7.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ASTM D1238
Arkema Group LOTADER® 4700 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride
LOTADER 4700 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized under high pressure in an autoclave process. Comonomer content is high. Due to its properties (reacti..
Melt Index of Compound 7.0 - 9.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 7.0 - 9.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ASTM D1238
Arkema Group LOTRYL® 20 MBG 08 Copolymer Ethylene - Methyl Acrylate
LOTRYL® 20MBG08 is a random copolymer of ethylene and methyl acrylate made by high-pressure radicalar polymerisation process. Due to the high methyl acrylate content, LOTRYL® 20 MBG 08 is a polyme..
Melt Index of Compound 7.0 g/10 min
7.0 g/10 min
ASTM D1238
Cheng Yu Plastic BK1021 Electric Conducting Polypropylene, Extrusion
Melt Index of Compound 7.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 7.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm3/10 min; ISO 1133
DuPont Performance Polymers Delrin® 577 BK000 Acetal Homopolymer  (Unverified Data**)
Delrin® 577 BK000 is a medium viscosity acetal homopolymer containing 20% glass fiber filler, with high stiffness, low warpage and low creep for superior performance at elevated temperature. It con..
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 7.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® 3412ECR PC (Asia Pacific)
Lexan* 3412ECR Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V0 rating and is available in v..