- Polymer Property : Melt Index of Compound = 7.0 g/10 min
Polymer Property : Melt Index of Compound = 7.0 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Index of Compound |
7.0
g/10 min @Load 5.00 kg, Temperature 190 °C |
7.0
g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
|
Polykemi AB POLYelast TPE Z506 Thermoplastic Elastomer, SEBS-based
Information provided by Polykemi AB
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 10.0 kg, Temperature 220 °C |
7.0
g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics GELOY FXW751SK ASA+PC (Asia Pacific)
Sparkle Metallic VisualFx ASA+PC Resin - Weatherable, High Heat & Impact Resin
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0
g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Lexan® 500ECR PC
Lexan* 500ECR Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. It is of non-chlorinated & non-brominated flame retardant systems with UL-94 V0 rating at 2.3mm. It is a..
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0
g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Lexan® HP6NR PC (Europe-Africa-Middle East)
Low/med flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains no ..
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0
g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Lexan® LUX9612G PC (Europe-Africa-Middle East)
Lexan LUX9612G (EXRL0945) is a UV stabilized high viscosity, flame retardant polycarbonate featuring non brominated and non chlorinated FR system with diffusion effect and thin wall FR performance p..
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0
g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Lexan® 955U PC (Europe-Africa-Middle East)
Lexan* 955U Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating and is UV stabilized, providing additio..
|
|||
| Melt Index of Compound | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 |
|
LyondellBasell Petrothene® GA616050 Linear Low Density Polyethylene
ApplicationsPETROTHENE GA 616-050 is a linear low density polyethylene resin which can be dry blended with low density polyethylene coating resins to produce linear low extrusion coatings. LDPE grad..
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 5.00 kg, Temperature 360 °C |
7.0
g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics ULTEM 2200F PEI
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 5.00 kg, Temperature 360 °C |
7.0
g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics ULTEM CRS5311 PEI (Europe-Africa-Middle East)
30% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. Resin is RoHS compliant. UL94 V0 and 5VA li..
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 5.00 kg, Temperature 250 °C |
7.0
g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Valox® IQ357 PBT+PC
Valox* Resin IQ357: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified.
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 5.00 kg, Temperature 250 °C |
7.0
g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Valox® IQ357M PBT+PC
Valox* Resin IQ357M: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified, easy flow product with mold release.
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 5.00 kg, Temperature 250 °C |
7.0
g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Valox® IQ357M PBT+PC (Asia Pacific)
Valox* Resin IQ357M: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified, easy flow product with mold release.
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 5.00 kg, Temperature 250 °C |
7.0
g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Valox® IQ357U PBT+PC
Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin.
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 5.00 kg, Temperature 250 °C |
7.0
g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Valox® IQ357U PBT+PC (Asia Pacific)
Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin.
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 5.00 kg, Temperature 265 °C |
7.0
g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Xenoy® X4870HH PC+PET (Asia Pacific)
Xenoy X4870HH is a high heat, very high modulus and ductile PC/PET blend. Furthermore this resin provides chemical resistance, very low creep, low CTE, excellent fatique and high heat dimensional st..
|
|||
| Melt Index of Compound | 7.0 g/10 min | 7.0 g/10 min | |
|
Sibur ABS-C Molding Grade ABS Plastic
With high resistance to burning for bodies of devices, technical articles and consumer goods, and contacting with good products.
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 10.0 kg, Temperature 280 °C |
7.0
g/10 min @Load 22.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics NORYL GFN3 PPE+HIPS (Europe-Africa-Middle East)
Noryl GFN3 is a standard 30 % glass filled material with a HDT/A of 145C according to ISO 75
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 5.00 kg, Temperature 280 °C |
7.0
g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics NORYL GTX GTX830 PPE+PA (Europe-Africa-Middle East)
NORYL GTX830 a 30% glass reinforced grade which offers an excellent combination of chemical/heat resistance in combination with stiffness.
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 5.00 kg, Temperature 280 °C |
7.0
g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA (Asia Pacific)
Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-..
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 2.16 kg, Temperature 280 °C |
7.0
g/10 min @Load 4.76 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics NORYL GTX GTX964W PPE+PS+PA
Noryl GTX* GTX964W resin is a blend of Polyphenylene Ether and Polyamide resin with very high impact and high flow. The material wsa designed for large parts, body panels, and thinwall applications..
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 5.00 kg, Temperature 280 °C |
7.0
g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics NORYL N300X PPE+PS
PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0. High heat. Dielectric strength. Dimensional stability. Suitable for E/E applications.
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 2.16 kg, Temperature 250 °C |
7.0
g/10 min @Load 4.76 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Valox® 430 PBT (Europe-Africa-Middle East)
VALOX 430 is 33% glass reinforced, impact modified PBT injection moulding resin.
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 2.16 kg, Temperature 265 °C |
7.0
g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Valox® V8090 PBT+PET (Europe-Africa-Middle East)
50% Glass Fiber Reinforced PBT-PET resin
|
|||
| Melt Index of Compound | 7.0 - 12 g/10 min | 7.0 - 12 g/10 min | |
|
Sibur Discar-E PC/ABS Compositional Polymer
Composition material PC/ABS with high shock resistance, thermal, light, and atmospheric resistance for profile articles of technical purpose and for sheets with following pneumatic formation of auto..
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 5.00 kg, Temperature 280 °C |
7.0
g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics NORYL ENV105 PPE+HIPS (Europe-Africa-Middle East)
NORYL ENV105 is an impact modified extrusion grade with a Vicat B/120 of 115C according ISO 306.
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 5.00 kg, Temperature 300 °C |
7.0
g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics NORYL GTX GTX678 PPE+PA (Asia Pacific)
Noryl GTX678 resin is a high performance blend of PPE/PA that exhibits an excellent balance on non-halogenated flame retardance, conductivity, ductility, and high-heat resistance. This grade can be..
|
|||
| Melt Index of Compound | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 |
|
A. Schulman POLYTROPE™ TPP 530 Injection Molding Grade Olefinic Thermoplastic Elastomer
DescriptionPolytrope TPP 530 is an injection molding grade olefinic thermoplastic elastomer. This mineral filled product is recommended for applications requiring high stiffness and low thermal exp..
|
|||
| Melt Index of Compound |
7.0
g/10 min @Load 2.16 kg, Temperature 190 °C |
7.0
g/10 min @Load 4.76 lb, Temperature 374 °F |
Condition E; ASTM D1238 |
|
A. Schulman LP390-01 Narrow Molecular Weight Copolymer
DescriptionLP 390-01 natural is a narrow molecular weight copolymer, high density polyethylene combining excellent impact strength with good environmental stress crack resistance.ApplicationLP 390-0..
|
|||
| Melt Index of Compound | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 |
|
DuPont Elvax® 750 Ethylene-Vinyl Acetate Copolymer Resin
Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with..
|
|||
| Melt Index of Compound |
7.0
-
9.0
g/10 min @Load 2.16 kg, Temperature 190 °C |
7.0
-
9.0
g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
|
Arkema Group LOTRYL® 20 MA 08 Copolymer Ethylene - Methyl Acrylate
LOTRYL® 20 MA 08 is a random copolymer of ethylene and methyl acrylate made by high-pressure radicalar polymerisation process. Due to the high methyl acrylate content, LOTRYL® 20 MA 08 is a polyme..
|
|||