SABIC Innovative Plastics Lexan® HPS6 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® HPS6 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Med/low flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam e-beam and gamma sterilizable. Contains mold release.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.35 % | 0.35 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| 112.2 g/10 min @Load 5.00 kg, Temperature 300 °C |
112.2 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 | |
| Melt Index of Compound | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
| 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 135 % | 135 % | Type I, 50 mm/min; ASTM D638 |
| 140 % | 140 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| 6.5 % | 6.5 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 |
| 2.31 GPa | 335 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 95.0 MPa | 13800 psi | 2 mm/min; ISO 178 |
| 97.0 MPa | 14100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.25 GPa | 326 ksi | 2 mm/min; ISO 178 |
| 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 9.07 J/cm | 17.0 ft-lb/in | ASTM D256 |
| 1.39 J/cm @Temperature -30.0 °C |
2.60 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 32.04 J/cm | 60.02 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | 80*10*3; ISO 180/1A |
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 7.50 J/cm² | 35.7 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 65.0 J @Temperature 23.0 °C |
47.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 62.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 57.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 60.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 140 °C | 284 °F | Rate B/120; ISO 306 |
| 143 °C | 289 °F | Rate B/50; ISO 306 | |
| 154 °C | 309 °F | Rate B/50; ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® A9860 TPE, ABS/PC Overmold
- SABIC Innovative Plastics Lexan® EXL8414 PC Copolymer
- Huntsman MY 721 Multifunctional Resin
- SABIC Innovative Plastics LNP Thermocomp MX96070 PP (Europe-Africa-Middle East)
- Styron XZ 97218.00 Styrene Acrylate
- Teknor Apex Telcar® TL-2717B Thermoplastic Elastomer
- Chosun Refractories BATN-3 Gas Purging Refractory
- C.O.I.M. DIEXTER® G196 Polyol Polyester
- BP Amoco Acclear® 6219 Homopolymer Polypropylene, High Clarity Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved