SABIC Innovative Plastics Lexan® HP4NR PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® HP4NR PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains no mold release.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.19 g/cc
0.0430 lb/in³
ASTM D792
1.19 g/cc
0.0430 lb/in³
ISO 1183
Water Absorption 0.15 %

@Time 86400 sec
0.15 %

@Time 24.0 hour
ASTM D570
Moisture Absorption 0.100 %
0.100 %
23°C / 50% RH; ISO 62
Moisture Absorption at Equilibrium 0.35 %
0.35 %
ASTM D570
0.58 %

@Temperature 100 °C
0.58 %

@Temperature 212 °F
ASTM D570
Water Absorption at Saturation 0.26 %
0.26 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 10.5 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10.5 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 70
70
ASTM D785
Hardness, Rockwell R 118
118
ASTM D785
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
73.0 MPa
10600 psi
50 mm/min; ISO 527
Tensile Strength, Yield 61.0 MPa
8850 psi
50 mm/min; ISO 527
62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 128 %
128 %
50 mm/min; ISO 527
130 %
130 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
50 mm/min; ISO 527
7.0 %
7.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.30 GPa
334 ksi
50 mm/min; ASTM D638
2.39 GPa
347 ksi
1 mm/min; ISO 527
Flexural Yield Strength 93.0 MPa
13500 psi
2 mm/min; ISO 178
96.0 MPa
13900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.25 GPa
326 ksi
2 mm/min; ISO 178
2.25 GPa
326 ksi
ISO 178
2.34 GPa
339 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 8.01 J/cm
15.0 ft-lb/in
ASTM D256
2.20 J/cm

@Temperature -30.0 °C
4.12 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 32.04 J/cm
60.02 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 70.0 kJ/m²
33.3 ft-lb/in²
80*10*3; ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 7.50 J/cm²
35.7 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.50 J/cm²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Tensile Impact Strength 577 kJ/m²
275 ft-lb/in²
Type S; ASTM D1822
Dart Drop, Total Energy 169 J
125 ft-lb
ASTM D3029
88.0 J

@Temperature 23.0 °C
64.9 ft-lb

@Temperature 73.4 °F
ASTM D3763
Taber Abrasion, mg/1000 Cycles 10
10
CS-17, 1 kg; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 68.4 µm/m-°C

@Temperature -40.0 - 95.0 °C
38.0 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
78.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
78.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 68.4 µm/m-°C

@Temperature -40.0 - 95.0 °C
38.0 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
76.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
76.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Specific Heat Capacity 1.25 J/g-°C
0.299 BTU/lb-°F
ASTM C351
Thermal Conductivity 0.190 W/m-K
1.32 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 137 °C

@Thickness 6.40 mm
279 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 127 °C
261 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
126 °C

@Thickness 3.20 mm
259 °F

@Thickness 0.126 in
unannealed; ASTM D648
132 °C

@Thickness 6.40 mm
270 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 143 °C
289 °F
Rate B/50; ISO 306
145 °C
293 °F
Rate B/120; ISO 306
154 °C
309 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 130 °C
266 °F
UL 746B
UL RTI, Mechanical with Impact 130 °C
266 °F
UL 746B
UL RTI, Mechanical without Impact 130 °C
266 °F
UL 746B
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+17 ohm-cm
>= 1.00e+17 ohm-cm
ASTM D257
Dielectric Constant 2.96

@Frequency 1.00e+6 Hz
2.96

@Frequency 1.00e+6 Hz
ASTM D150
3.17

@Frequency 50.0 - 60.0 Hz
3.17

@Frequency 50.0 - 60.0 Hz
ASTM D150
Dielectric Strength 14.9 kV/mm

@Thickness 3.20 mm
378 kV/in

@Thickness 0.126 in
in air; ASTM D149
Dissipation Factor 0.00090

@Frequency 50.0 - 60.0 Hz
0.00090

@Frequency 50.0 - 60.0 Hz
ASTM D150
0.010

@Frequency 1.00e+6 Hz
0.010

@Frequency 1.00e+6 Hz
ASTM D150
Comparative Tracking Index 250 - 400 V
250 - 400 V
UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI 60 - 120 arcs
60 - 120 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 25.4 - 80.0 mm/min
1.00 - 3.15 in/min
UL 746A