Mitsubishi Hostaphan® RN, 190 micron Nominal Thickness Universal Polyethylene Terephthalate Film

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Unreinforced
Manufacturer Mitsubishi
Trade Name Hostaphan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mitsubishi Hostaphan® RN, 190 micron Nominal Thickness Universal Polyethylene Terephthalate Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hostaphan® RN is a biaxially oriented film made of polyethylene terephthalate (PET) and characterized by outstanding physical properties.Applications:Films for industrial applicationsCoatingLaminatingMetallizingPrintingDecorative filmsGloss laminationsAdhesive tapesAdhesive filmsInsulation tapesElectrical insulationFlexible printed circuitsTransformers and coilsReprographyBase for color printingCarrier film for flexible printing platesDrafting film/engineering
Physical Properties Metric English Comments
Density 1.40 g/cc

@Temperature 23.0 °C
 0.0506 lb/in³

@Temperature 73.4 °F
 ASTM D1505-68, method C
Water Absorption 0.50 %

@Temperature 23.0 °C
 0.50 %

@Temperature 73.4 °F
 4 days in water; ASTM D570
Linear Mold Shrinkage 0.010 cm/cm

@Temperature 150 °C,
Time 900 sec
 0.010 in/in

@Temperature 302 °F,
Time 0.250 hour
 DIN 40634
Linear Mold Shrinkage, Transverse 0.0030 cm/cm

@Temperature 150 °C,
Time 900 sec
 0.0030 in/in

@Temperature 302 °F,
Time 0.250 hour
 DIN 40634
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 150 MPa
21800 psi
Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Tensile Strength at Yield, TD 200 MPa
29000 psi
Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Elongation at Break, MD >= 200 %
>= 200 %
Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Elongation at Break, TD 140 %
140 %
Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Modulus of Elasticity 3.60 GPa

@Temperature 23.0 °C
 522 ksi

@Temperature 73.4 °F
 MD; Test speed 1%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
4.30 GPa

@Temperature 23.0 °C
 624 ksi

@Temperature 73.4 °F
 TD; Test speed 1%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Coefficient of Friction, Static 0.40
0.40
DIN 53375 or ASTM D1894
Optical Properties Metric English Comments
Haze 25 %
25 %
Enlarged measurement angle; ASTM D1003-61, method A
Electrical Properties Metric English Comments
Dielectric Constant 2.9

@Frequency 2.40e+8 Hz,
Temperature 23.0 °C
 2.9

@Frequency 2.40e+8 Hz,
Temperature 73.4 °F
 DIN 40634 or VDE 0345 in air
2.9

@Frequency 9.30e+9 Hz,
Temperature 23.0 °C
 2.9

@Frequency 9.30e+9 Hz,
Temperature 73.4 °F
 DIN 40634 or VDE 0345 in air
3.2

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 3.2

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 DIN 40634 or VDE 0345 in air
3.3

@Frequency 50.0 Hz,
Temperature 23.0 °C
 3.3

@Frequency 50.0 Hz,
Temperature 73.4 °F
 DIN 40634 or VDE 0345 in air
3.3

@Frequency 1000 Hz,
Temperature 23.0 °C
 3.3

@Frequency 1000 Hz,
Temperature 73.4 °F
 DIN 40634 or VDE 0345 in air
3.6

@Frequency 50.0 Hz,
Temperature 150 °C
 3.6

@Frequency 50.0 Hz,
Temperature 302 °F
 DIN 40634 or VDE 0345 in air
Dielectric Strength 450 kV/mm

@Temperature 23.0 °C
 11400 kV/in

@Temperature 73.4 °F
 DC; DIN 40634 or VDE 0345 in air
135 kV/mm

@Frequency 50.0 Hz,
Temperature 150 °C
 3430 kV/in

@Frequency 50.0 Hz,
Temperature 302 °F
 DIN 40634 or VDE 0345 in air
150 kV/mm

@Frequency 50.0 Hz,
Temperature 23.0 °C
 3810 kV/in

@Frequency 50.0 Hz,
Temperature 73.4 °F
 DIN 40634 or VDE 0345 in air
Descriptive Properties Value Comments
Conductivity of Aqueous Extract (µS/cm) 2
DIN 40634 or VDE 0345; 1 kHz
F5-value (MPa) 105
ISO 527-1, ISO 527-3; Sample type 2; MD; Test speed 100%/min.; 23ºC, 50% r.h.
105
ISO 527-1, ISO 527-3; Sample type 2; TD; Test speed 100%/min.; 23ºC, 50% r.h.
Frigen Extract (%) 0.05
DIN 8944; Cold extraction
Trichloroethylene- Extract (%) 0.2
DIN 8943; Extracted in Soxhalet apparatus for 2h. Boiled down for 15h at 105ºC