SABIC Innovative Plastics LNP Thermocomp AF0029 ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp AF0029 ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* AF0029 is an ABS base resin containing Glass Fiber. Characteristics of this grade are Flame Retardancy.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.28 g/cc
1.28 g/cc
ASTM D 792
Density 1.27 g/cc
0.0459 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.30 %
0.30 %
23°C / 50% RH; ISO 62
0.19 %

@Time 86400 sec
 0.19 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Time 86400 sec
 0.0030 - 0.0050 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Time 86400 sec
 0.0040 - 0.0060 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa
10200 psi
5 mm/min; ISO 527
71.0 MPa
10300 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 70.0 MPa
10200 psi
5 mm/min; ISO 527
71.0 MPa
10300 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
2.1 %
2.1 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 2.0 %
2.0 %
5 mm/min; ISO 527
2.1 %
2.1 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 5.04 GPa
731 ksi
1 mm/min; ISO 527
5.49 GPa
796 ksi
50 mm/min; ASTM D 638
Flexural Strength 100 MPa
14500 psi
ISO 178
110 MPa
16000 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Yield Strength 110 MPa
16000 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 4.52 GPa
656 ksi
2 mm/min; ISO 178
4.81 GPa
698 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.430 J/cm

@Temperature 23.0 °C
 0.806 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 2.77 J/cm

@Temperature 23.0 °C
 5.19 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 17.0 kJ/m²

@Temperature 23.0 °C
 8.09 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
5.00 J

@Temperature 23.0 °C
 3.69 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 4.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
 2.22 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 10.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 5.56 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
105 °C

@Thickness 3.20 mm
 221 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 97.0 °C
207 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
97.0 °C

@Thickness 3.20 mm
 207 °F

@Thickness 0.126 in
 unannealed; ASTM D 648