SABIC Innovative Plastics Xylex X8300HP PC+POLYESTER (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xylex |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xylex X8300HP PC+POLYESTER (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparent, US Food Contact compliant, chemically resistant.
This grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HX8300HP.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 265 °C |
15 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D 1238 |
| 15 g/10 min @Load 2.16 kg, Temperature 265 °C |
15 g/10 min @Load 4.76 lb, Temperature 509 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 73 | 73 | 10S reading; ASTM D 2240 |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D 638 |
| 54.0 MPa | 7830 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D 638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 150 % | 150 % | Type I, 50 mm/min; ASTM D 638 |
| >= 200 % | >= 200 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D 638 |
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 1.52 GPa | 220 ksi | 50 mm/min; ASTM D 638 |
| 1.60 GPa | 232 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 78.0 MPa | 11300 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 71.0 MPa | 10300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 1.68 GPa | 244 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 1.70 GPa | 247 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 11.2 J/cm @Temperature 23.0 °C |
21.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Impact Test | 95.0 J @Temperature 23.0 °C |
70.1 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| 105 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| 105 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | ISO 8302 |
| Hot Ball Pressure Test | <= 85.0 °C | <= 185 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 79.0 °C @Thickness 3.20 mm |
174 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 75.0 °C @Thickness 3.20 mm |
167 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 96.0 °C | 205 °F | Rate B/50; ASTM D 1525 |
| 96.0 °C | 205 °F | Rate B/120; ISO 306 | |
| Glow Wire Test | 750 °C @Thickness 1.00 mm |
1380 °F @Thickness 0.0394 in |
Glow Wire Flammability Index; IEC 60695-2-12 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.539 | 1.539 | ISO 489 |
| Haze | 1.0 % @Thickness 2.54 mm |
1.0 % @Thickness 0.100 in |
ASTM D 1003 |
| Transmission, Visible | 88 % @Thickness 2.54 mm |
88 % @Thickness 0.100 in |
ASTM D 1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D 257 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ASTM D 257 |
| Comparative Tracking Index | >= 600 V | >= 600 V | PLC code 0; UL 746A |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 20 LS PA6, 20% glass beads, light stability
- SABIC Innovative Plastics Lexan® FXM121R PC (Europe-Africa-Middle East)
- Kennametal Stellite Stellite® 6 PM cast
- MetalTek MTEK 150 Cast UNS C95220 Aluminum Bronze
- Hexcel® HexPly® M48 180°C/356°F Curing Epoxy Matrix, M48/42%/G1094/1000
- Dow Corning SYL-OFF® SL 7688 CROSSLINKER
- CLAL-MSX NICLAL 3444 H14 4/4 Hard Copper Alloy, diameter < 8 Copper Alloy, Free Cutting Bronze
- Adell EL-16 Homopolymer Polypropylene, 30% Mineral Filled; Glass Reinforced
- UBE UBESTA® 3030U Nylon 12 (After Sodium Hydroide for 1000 hours)
- Arlon 44278R018 0.018" Uncured/Cured/Uncured Silicone Rubber Laminate with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved