- Polymer Property : Flexural Strength = 16000 psi
Polymer Property : Flexural Strength = 16000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| PolyOne Nymax™ GB 1200 30 HS BLACK 18 Polyamide 66 (Nylon 66) Preliminary Data SheetMolded Test Bars: Dry as MoldedInformation provided by PolyOne |
|||
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Owens Corning Glass Fiber Reinforced Polycarbonate, 10 wt.% glass Data provided by the manufacturer, Owens Corning. |
|||
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Niche Polymer PA66BK Nylon 66 Information provided by Niche Polymer |
|||
| Flexural Strength | 110 MPa | 16000 psi | STN EN ISO 178 |
| Plastcom SLOVAMID 6 G 10 Polyamide 6, 10% Graphite FeaturesPA 6 for injection moulding with addition of 10% graphite, the PA surface rolling resistance force is significantly lowered. Used mainly in the product of crates and cases for bearings, sli.. |
|||
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, at 50% RH
(discontinued **) AMODEL ET-1001 L resin is an impact modified polyphthalamide (PPA) with exceptional impact strength and practical toughness. AMODEL PPA resins offer high fatigue strength, and good chemical resistan.. |
|||
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| PolyOne Lubri-Tech™ NL-20GF/05T Nylon 6/12, Glass Filled, PTFE Lubricated
(discontinued **) Description/Features:Glass Fiber ReinforcedPTFE LubricatedInformation provided by PolyOne Corporation. |
|||
| Flexural Strength | 110 MPa | 16000 psi | |
| Lehmann & Voss LUVOCOM® 1-1120 Polyamide 66, with PTFE, lubricant modified, high viscosity Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
| Flexural Strength | 110 MPa | 16000 psi | |
| Lehmann & Voss LUVOCOM® 1502-7867/BL4 PPSU, unreinforced Applications: Automotive industry, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceHigh chemical res.. |
|||
| Flexural Strength | 110 MPa | 16000 psi | |
| Lehmann & Voss LUVOCOM® 19-7827 Polyamide 46, with PTFE, easy flowing Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
| Flexural Strength | 110 MPa | 16000 psi | ISO 178 |
| Grupo Repol Dinalon® A1X25 V0 PA66, V0 red phosphorus and halogen free Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
| Flexural Strength | 110 MPa | 16000 psi | ISO 178 |
| Mitsubishi Xantar® MX 1094 Polycarbonate-9% Glass Reinforced Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Flexural Strength | 110 MPa @Strain 5.50 % |
16000 psi @Strain 5.50 % |
d.a.m., 2 mm/min; ISO 178-A |
| Lanxess Durethan® B 30 S F30 000000 Nylon 6, Flame Retardant PA 6, non-reinforced, injection molding, flame retardantInformation provided by LANXESS. |
|||
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Mitsui APELâ„¢ APL6013T Cyclo Olefin Copolymer (COC) This material possesses many characteristics inherent in polyolefins such as excellent electrical insulating properties and outstanding moisture resistance. In addition, it features good melt proces.. |
|||
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer LNP* LUBRICOMP* KCL34A is a compound based on Acetal Homopolymer resin containing 15% PTFE, 20% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive. |
|||
| Flexural Strength | 110 MPa | 16000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Valox® 771 PBT 35% mineral/glass reinforced flame retardant grade with a CTI performance level class of 0 rating. Applications which may see electrical arcing. |
|||
| Flexural Strength | 110 MPa | 16000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Valox® 771 PBT (Europe-Africa-Middle East) VALOX 771 is a 15% glass and 20% mineral filled, flame retarded injection moulding PBT resin. |
|||
| Flexural Strength | >= 110 MPa | >= 16000 psi | GB/T 9341-2008 |
| Sichuan Deyang Haton® hb DL Polyphenylene Sulfide Resin Extrusion, low chlorineInformation provided by Sichuan Deyang Chemical Co., LTD |
|||
| Flexural Strength | 110 MPa | 16000 psi | GB/T 9341-2008 |
| Sichuan Deyang Haton® hFR31 PPS / AR Polyphenylene Sulfide Injection molding, conductiveInformation provided by Sichuan Deyang Chemical Co., LTD |
|||
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Techmer ES Electrablend® PA6/6 03002 A MB Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement/Unspecified Filler/Reinfor.Additive: Lubricant, Impact Modifier and Heat StabilizerFeatures: Lubricated, Elec.. |
|||
| Flexural Strength | 110 MPa | 16000 psi | ISO 178-93 |
| Wellman Wellamid® GF10-66/6-LI6-NBK4 10% Glass Reinforced, Toughened Nylon 66/6 Description: Glass Reinforced, Toughened Nylon 66/6Information provided by Wellman. |
|||
| Flexural Strength | 110 MPa | 16000 psi | ISO 178-93 |
| Wellman Wellamid® NY1718-N1 General Purpose Nylon 6 Description: General Purpose Nylon 6Information provided by Wellman. |
|||
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| A. Schulman POLYFLAM™ E-13030B Reinforced Super Coupled Polypropylene Black DescriptionPolyfort® E-13030B is a reinforced super coupled polypropylene black. Information provided by A. Schulman. |
|||
| Flexural Strength | 110 MPa | 16000 psi | dry; ISO 178 |
| DSM Novamid® 1011CH5KR PA6 Heat Stabilized, Easy Molding Grade |
|||
| Flexural Strength | >= 110 MPa | >= 16000 psi | Perpendicular to laminations; IEC 1212-2 5.1 |
| Hippe EP PC 301 Woven Polyester Cloth Reinforced Epoxy Resin - Sheet Used in electrical and mechanical applications. Good resistance to SF6.Information provided by Hippe. |
|||
| Flexural Strength | 110 - 138 MPa | 16000 - 20000 psi | |
| Bulk Molding Compounds BMC 600LS Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 600LS molding compound is a low-shrink, Mineral filled, glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is a general purpose materia.. |
|||
| Flexural Strength | 110 MPa | 16000 psi | At Rupture; ASTM D790 |
| Sumitomo Bakelite North America FS-5 Short-Glass Reinforced Diallyl Phthalate Short glass fiber reinforced, non-flame retardant, diallyl meta-phthalate molding compound which meets the requirements of ASTM D5948 TYPE SIG.Information provided by Vyncolit, a Sumitomo Bak Group |
|||