SABIC Innovative Plastics Cycoloy® C1110 PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® C1110 PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High impact and ductility at 73F (23C) and -20F (-29C).
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ASTM D792
Water Absorption 0.10 %

@Time 86400 sec
 0.10 %

@Time 24.0 hour
 ASTM D570
Moisture Absorption at Equilibrium 0.40 %
0.40 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 2.5 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 2.5 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
8.0 g/10 min

@Load 3.80 kg,
Temperature 260 °C
 8.0 g/10 min

@Load 8.38 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 56.0 MPa
8120 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 150 %
150 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.20 GPa
319 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 86.0 MPa
12500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.34 GPa
339 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 6.40 J/cm
12.0 ft-lb/in
ASTM D256
5.34 J/cm

@Temperature -30.0 °C
 10.0 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Dart Drop, Total Energy 40.0 J

@Temperature -30.0 °C
 29.5 ft-lb

@Temperature -22.0 °F
 ASTM D3763
54.0 J

@Temperature 23.0 °C
 39.8 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 123 °C

@Thickness 3.20 mm
 253 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 107 °C

@Thickness 3.20 mm
 225 °F

@Thickness 0.126 in
 unannealed; ASTM D648
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.21 mm
 HB

@Thickness 0.0476 in
 UL 94
Electrical Properties Metric English Comments
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten; ASTM D495
Comparative Tracking Index 175 - 250 V
175 - 250 V
UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 10.0 - 25.4 mm/min
0.394 - 1.00 in/min
UL 746A
Descriptive Properties Value Comments
UV-light, water exposure/immersion F2
UL 746C