- Sumitomo Bakelite North America RX® 1-501N Mineral Filled Diallyl Phthalate
Sumitomo Bakelite North America RX® 1-501N Mineral Filled Diallyl Phthalate
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP), Cast, Mineral Filler , Filled/Reinforced Thermoset |
| Manufacturer | Sumitomo Bakelite North America |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite North America RX® 1-501N Mineral Filled Diallyl Phthalate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mineral filled diallyl ortho-phthalate molding compound which meets the requirements of ASTM D5948 Type MDG.Information provided by Vyncolit, a Sumitomo Bak Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | Relative Density; ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | Compression Molding; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.2 MPa | 8010 psi | ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | At Rupture; ASTM D790 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | ASTM D790 |
| Compressive Strength | 145 MPa | 21000 psi | ASTM D695 |
| Izod Impact, Notched | 0.240 J/cm | 0.450 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature 20.0 °C |
13.9 µin/in-°F @Temperature 68.0 °F |
ASTM E-831 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | UL 746B |
| Deflection Temperature at 1.8 MPa (264 psi) | 166 °C | 331 °F | As molded; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz |
3.6 @Frequency 1e+6 Hz |
Wet; ASTM D150 |
| 4.2 @Frequency 1000 Hz |
4.2 @Frequency 1000 Hz |
wet; ASTM D150 | |
| Dielectric Strength | 15.8 kV/mm | 401 kV/in | 60Hz, Step-by-Step, wet; ASTM D149 |
| Dissipation Factor | 0.013 @Frequency 1000 Hz |
0.013 @Frequency 1000 Hz |
wet; ASTM D150 |
| 0.014 @Frequency 1e+6 Hz |
0.014 @Frequency 1e+6 Hz |
wet; ASTM D150 | |
| Arc Resistance | 140 sec | 140 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black, Blue, Brown, Green, Red | |
| Form | Granular | |
| Main Filler | Mineral | |
| Molding Method | Compression, transfer, injection |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 H-KV30 Nylon 6 for injection molding, 30% glass ball reinforced
- PolyOne Edgetek® SY-15GB/000 Polystyrene (PS), Glass Bead Filled (discontinued **)
- Sichuan Deyang Haton® hb Polyphenylene Sulfide Resin
- Styron CALIBREâ„¢ 603 3 Polycarbonate, Branched
- Teknor Apex Monprene® MP-2322UV Thermoplastic Elastomer
- A. Schulman PP 1329H-01 Polypropylene Medium Impact Polypropylene
- Dow Corning SYL-OFF® PMCPSL 600 Coating
- Braskem Prisma 2400 RACO Random Polypropylene Copolymer
- BASF Ultramid® A3EG3 15% Glass Filled PA66 (Conditioned)
- SABIC Innovative Plastics LNP Verton WV007XXP PBT (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved