| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hostacom™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hostacomâ„¢ RTA3184 Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hostacomâ„¢ RTA3184 medium melt flow, 1,300 MPa flexural modulus, low level glass-reinforced, colorable, interior trim grade thermoplastic elastomeric olefin (TEO) resin is modified to provide balanced rigidity, dimensional stability and processability. It was designed for a variety of molded-in color automotive interior trim components. Uses: Automotive interior partsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D792 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 68 | 68 | ISO 868 |
| Tensile Strength, Yield | 21.4 MPa | 3100 psi | ASTM D 638 |
| 23.0 MPa | 3340 psi | ISO 527-1, 2 | |
| Elongation at Break | 350 % | 350 % | ASTM D 638 |
| Elongation at Yield | 8.0 % | 8.0 % | ISO 527-1, -2 |
| Flexural Modulus | 1.17 GPa | 170 ksi | Tangent, 0.05 in/min; ASTM D790 |
| 1.30 GPa | 189 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 2.50 kJ/m² @Temperature -40.0 °C |
1.19 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 3.50 kJ/m² @Temperature 0.000 °C |
1.67 ft-lb/in² @Temperature 32.0 °F |
ISO 180 | |
| 11.0 kJ/m² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Gardner Impact | 5.01 J @Temperature -30.0 °C |
3.69 ft-lb @Temperature -22.0 °F |
ASTM D3029 |
| 20.0 J @Temperature 23.0 °C |
14.7 ft-lb @Temperature 73.4 °F |
ASTM D3029 | |
| Tear Strength | 123 kN/m | 700 pli | ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature -30.0 - 100 °C |
44.4 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 92.2 °C | 198 °F | Unannealed; ASTM D648 |
| 100 °C | 212 °F | Unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | Unannealed; ISO 75A-1, -2 |
| Shrinkage | 1.3 % | 1.3 % | Tool, 100x150x3.2 mm, injection molded plaque; Basell Test Method |
| 1.60 % @Temperature 121 °C, Time 3600 sec |
1.60 % @Temperature 250 °F, Time 1.00 hour |
Afterbake, 100x150x3.2 mm; Basell Method |
Users viewing this material also viewed the following:
- Northstar Polymers PPA-059 Curing Agent
- PolyOne Geon™ Vinyl Dry Blend E7364 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Polimeri Europa EDISTIR PD RR745E High Impact Polystyrene (HIPS) (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP RX94033 PA6.6 (Europe-Africa-Middle East)
- Techmer ES Plastiblend® ABS 8004 UV MB
- Dow Corning MOLYKOTE® AS-810 GREASE
- Carpenter Speed Star® High Speed Steel (Red-Hard) (AISI M2)
- 3M 7945MP Hi-Performance Acrylic 200MP
- Borealis LE7710 Polyethylene Compound, Semiconductive, Thermoplastic
Copyright © lookpolymers.com All Rights Reserved