Styron PulseÂ® 759 ABS + Polycarbonate, 15% Glass Reinforced

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC)
Manufacturer	Styron
Trade Name	Pulse®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styron PulseÂ® 759 ABS + Polycarbonate, 15% Glass Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PULSEÂ® 759 Engineering resin is a 15% glass reinforced resin designed to provide excellent processability, high heat resistance, and practical toughness. PULSE 759 Engineering resin has been used in automotive interior trim applications.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.

Physical Properties	Metric	English	Comments
Density	1.22 g/cc	0.0441 lb/inÂ³	ASTM Data
Melt Density	0.962 g/cc	0.0348 lb/inÂ³	Melt density
Water Absorption	0.15 %	0.15 %
Moisture Absorption at Equilibrium	0.32 %	0.32 %	Humidity Absorption
Linear Mold Shrinkage	0.0025 cm/cm	0.0025 in/in
Melt Flow	2.4 g/10 min @Load 3.80 kg, Temperature 230 Â°C	2.4 g/10 min @Load 8.38 lb, Temperature 446 Â°F	ASTM Data

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120
Tensile Strength, Ultimate	82.7 MPa	12000 psi	ASTM Data
Tensile Strength, Yield	82.7 MPa	12000 psi	ASTM Data
Elongation at Break	2.6 %	2.6 %	ASTM Data
Izod Impact, Notched	1.12 J/cm	2.10 ft-lb/in	ASTM Data
	0.854 J/cm @Temperature -50.0 Â°C	1.60 ft-lb/in @Temperature -58.0 Â°F	ASTM Data
Impact Test	6.22 J @Temperature -30.0 Â°C	4.59 ft-lb @Temperature -22.0 Â°F	Instrumented Dart Total Energy
	11.3 J @Temperature 23.0 Â°C	8.33 ft-lb @Temperature 73.4 Â°F	Instrumented Dart Total Energy

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	57.6 Âµm/m-Â°C @Temperature 20.0 Â°C	32.0 Âµin/in-Â°F @Temperature 68.0 Â°F	ASTM data
Specific Heat Capacity	1.66 J/g-Â°C	0.397 BTU/lb-Â°F
Thermal Conductivity	0.142 W/m-K	0.985 BTU-in/hr-ftÂ²-Â°F
Deflection Temperature at 1.8 MPa (264 psi)	116 Â°C	241 Â°F	Unannealed; 127Â°C (261Â°F) annealed; ASTM Data
Vicat Softening Point	138 Â°C	280 Â°F