SABIC Innovative Plastics Cycolac® FR15U ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycolac®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycolac® FR15U ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flame retardant ABS. Excellent indoor UV properties. Excellent moldability. UL94 V-0/5VA rated.ing.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Viscosity 320000 cP
320000 cP
Melt Viscosity, 200°C, 1000 sec-1; ASTM D3825
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 3.3 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 3.3 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
7.0 g/10 min

@Load 5.00 kg,
Temperature 220 °C
 7.0 g/10 min

@Load 11.0 lb,
Temperature 428 °F
 ISO 1133
Melt Index of Compound 40 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 40 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 30.0 MPa
4350 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 37.0 MPa
5370 psi
Type I, 5 mm/min; ASTM D638
41.0 MPa
5950 psi
50 mm/min; ISO 527
Elongation at Break 17 %
17 %
Type I, 5 mm/min; ASTM D638
21.9 %
21.9 %
50 mm/min; ISO 527
Elongation at Yield 2.4 %
2.4 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 2.06 GPa
299 ksi
5 mm/min; ASTM D638
2.21 GPa
321 ksi
1 mm/min; ISO 527
Flexural Yield Strength 63.0 MPa
9140 psi
2 mm/min; ISO 178
67.0 MPa
9720 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.26 GPa
328 ksi
2 mm/min; ISO 178
2.34 GPa
339 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 2.13 J/cm
3.99 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
80*10*4; ISO 180/1A
Dart Drop, Total Energy 28.0 J

@Temperature 23.0 °C
 20.7 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 50.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 91.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 51.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 86.0 °C

@Thickness 3.20 mm
 187 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C

@Thickness 3.20 mm
 167 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 92.0 °C
198 °F
Rate B/50; ISO 306
93.0 °C
199 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.49 mm
 V-0

@Thickness 0.0587 in
 UL 94
5VA

@Thickness 2.79 mm
 5VA

@Thickness 0.110 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
IEC 60093
Dielectric Strength 20.0 kV/mm

@Thickness 3.20 mm
 508 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
Arc Resistance 0.00 - 60 sec
0.00 - 60 sec
Tungsten; ASTM D495
Comparative Tracking Index 400 - 600 V
400 - 600 V
UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI 0.00 - 15 arcs
0.00 - 15 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL 746A