Lucas-Milhaupt BRAZE 999 Commercial Grade Fine Silver
| Category | Metal , Nonferrous Metal , Precious Metal , Silver Alloy , Solder/Braze Alloy , Pure Element |
| Manufacturer | Lucas-Milhaupt |
| Trade Name | BRAZE |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucas-Milhaupt BRAZE 999 Commercial Grade Fine Silver.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Commercial grade fine silver (99.90% minimum silver) is widely used in numerous electrical, electronic, and industrial applications, such as contacts, fuse elements, lead wires, battery plated, and rupture discs. Fine silver is generally selected for its high thermal and electrical conductivity, as well as for its good resistance to oxidation and corrosive attack. It also exhibits excellent ductility and is easily joined by welding or brazing. Information provided by Lucas-Milhaupt, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 10.49 g/cc | 0.3790 lb/in³ | |
| Vapor Pressure | 0.00133 bar @Temperature 1360 °C |
1.00 torr @Temperature 2480 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 165 - 207 MPa | 24000 - 30000 psi | Wire, Temper-Soft |
| 165 - 207 MPa | 24000 - 30000 psi | Strip, Temper-Soft | |
| 179 - 228 MPa | 26000 - 33000 psi | Strip, Temper-1/4 Hard | |
| 207 - 255 MPa | 30000 - 37000 psi | Strip, Temper-1/2 Hard | |
| 207 - 255 MPa | 30000 - 37000 psi | Wire, Temper- 1/4 Hard | |
| 255 - 303 MPa | 37000 - 44000 psi | Strip, Temper-Hard | |
| 269 - 317 MPa | 39000 - 46000 psi | Wire, Temper- 1/2 Hard | |
| 283 - 324 MPa | 41000 - 47000 psi | Strip, Temper-Ex. Hard | |
| 290 - 338 MPa | 42000 - 49000 psi | Wire, Temper- Hard | |
| 303 - 352 MPa | 44000 - 51000 psi | Strip, Temper-Spring | |
| 317 - 365 MPa | 46000 - 53000 psi | Wire, Temper-Ex. Hard | |
| 324 - 372 MPa | 47000 - 54000 psi | Wire, Temper-Spring | |
| 331 - 379 MPa | 48000 - 55000 psi | Strip, Temper-Ex. Spring | |
| 331 - 379 MPa | 48000 - 55000 psi | Wire, Temper-Ex. Spring | |
| Elongation at Break | >= 1.0 % | >= 1.0 % | % in 2", Strip, Temper-Spring |
| >= 1.0 % | >= 1.0 % | % in 2", Strip, Temper-Ex. Spring | |
| >= 1.0 % | >= 1.0 % | % in 2", Wire, Temper-Spring | |
| >= 1.0 % | >= 1.0 % | % in 2", Wire, Temper- Ex. Spring | |
| >= 2.0 % | >= 2.0 % | % in 2", Strip, Temper-Ex. Hard | |
| >= 2.0 % | >= 2.0 % | % in 2", Wire, Temper- Hard | |
| >= 2.0 % | >= 2.0 % | % in 2", Wire, Temper- Ex. Hard | |
| >= 3.0 % | >= 3.0 % | % in 2", Strip, Temper- Hard | |
| >= 4.0 % | >= 4.0 % | % in 2", Wire, Temper- 1/4 Hard | |
| >= 4.0 % | >= 4.0 % | % in 2", Wire, Temper- 1/2 Hard | |
| >= 8.0 % | >= 8.0 % | % in 2", Strip, Temper-1/2 Hard | |
| >= 18 % | >= 18 % | % in 2", Strip, Temper- 1/4 Hard | |
| >= 25 % | >= 25 % | % in 2", Strip, Temper-Soft | |
| >= 25 % | >= 25 % | % in 2", Wire, Temper-Soft | |
| Reduction of Area | 0.00 % | 0.00 % | Strip, Temper-Soft |
| 0.00 % | 0.00 % | Wire, Temper-Soft | |
| 11 % | 11 % | Strip, Temper-1/4 Hard | |
| 21 % | 21 % | Strip, Temper-1/2 Hard | |
| 21 % | 21 % | Wire, Temper-1/4 Hard | |
| 37 % | 37 % | Wire, Temper-1/2 Hard | |
| 37 % | 37 % | Strip, Temper-Hard | |
| 50 % | 50 % | Strip, Temper- Ex. Hard | |
| 60 % | 60 % | Strip, Temper-Spring | |
| 60 % | 60 % | Wire, Temper- Hard | |
| 69 % | 69 % | Strip Temper, Ex. Spring | |
| 75 % | 75 % | Wire, Temper-Ex. Hard | |
| 84 % | 84 % | Wire, Temper-Spring | |
| 90 % | 90 % | Wire, Temper-Ex. Spring |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 19.0 µm/m-°C @Temperature 0.000 - 100 °C |
10.6 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Specific Heat Capacity | 0.2343 J/g-°C @Temperature 20.0 °C |
0.05600 BTU/lb-°F @Temperature 68.0 °F |
|
| Thermal Conductivity | 418 W/m-K @Temperature 20.0 °C |
2900 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
| Melting Point | 960.8 °C | 1761 °F | |
| Boiling Point | 2210 °C | 4010 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | <= 0.0020 % | <= 0.0020 % | |
| Bismuth, Bi | <= 0.0010 % | <= 0.0010 % | |
| Cadmium, Cd | <= 0.0050 % | <= 0.0050 % | |
| Copper, Cu | <= 0.080 % | <= 0.080 % | |
| Iron, Fe | <= 0.0050 % | <= 0.0050 % | |
| Lead, Pb | <= 0.025 % | <= 0.025 % | |
| Nickel, Ni | <= 0.0020 % | <= 0.0020 % | |
| Other, total | <= 0.15 % | <= 0.15 % | |
| Silver, Ag | >= 99.95 % | >= 99.95 % | |
| Zinc, Zn | <= 0.0050 % | <= 0.0050 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000001642 ohm-cm @Temperature 20.0 °C |
0.000001642 ohm-cm @Temperature 68.0 °F |
| Chemical Properties | Metric | English | Comments |
|---|---|---|---|
| Atomic Mass | 107.87 | 107.87 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 GF 40 PA66, 40% glass fibre
- Pyrotek R-3 Braided Glass Rope
- Mo-Sci Corporation GL-0176 Barium-Titanate Glass Spheres
- Techmer ES Plaslube® J-4/30/TF/13/SI/2 NAT PA6/12
- Sinotek Materials ZSKP32 Expandable Graphite
- Formosa Plastics Formolon® 113 PVC
- A. Schulman POLYBATCH™ Yellow 2600V Concentrate Based In Polyethylene
- A.D. Compound Adene NTFAG Copolymer 20% Talc Filled Polypropylene
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 60 PHR Carbon Black, N-990 (MT)
- Weartech International WT-25 Cobalt Hardfacing & Wear Resistant Alloy
Copyright © lookpolymers.com All Rights Reserved