- RheTech Products GC30P200-523 30% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, UV Stabilized, (GM 167A) Ebony
RheTech Products GC30P200-523 30% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, UV Stabilized, (GM 167A) Ebony
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products GC30P200-523 30% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, UV Stabilized, (GM 167A) Ebony.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Window frameHead lamp housingInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 30 % | 30 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | ASTM D955 |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 74 | 74 | ASTM D2240 |
| Tensile Strength at Break | 65.5 MPa | 9500 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 4.41 GPa | 640 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 2.03 J/cm @Temperature 23.0 °C |
3.80 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 1.80 J | 1.33 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 310 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Middle Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Front Barrel Temperature | 216 - 243 °C | 420 - 470 °F | |
| Nozzle Temperature | 221 - 232 °C | 430 - 450 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers FOMBLIN® Z60 PFPE Lubricant
- Silberline Dedusted Flake Series DF-2750 Aluminum Flake
- Borealis BB108E Polypropylene compound for Steel Pipe Coating
- Unifrax Fiberfrax® LDS Moldable Moldable Insulation
- Cytec (Conap) FR-1274 Conapoxy® Resin / Conacure® Hardener
- Fainplast Compounds GA 75/R Flexible PVC, Flame Retardant Sheathing
- Ascend Performance Materials Vydyne® R220/R228 Nylon 66, 40% Mineral Reinforced, Conditioned (2.5% Moisture)
- A. Schulman ComAlloy Comtuf® 613 Nylon 6, Glass Reinforced, Impact Modified
- Ashley Polymers Ashlene® 833 Nylon 6
Copyright © lookpolymers.com All Rights Reserved