RheTech Products GC10P100-01 10% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Black
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Glass Fiber Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products GC10P100-01 10% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Air ducts - distributionFuel filler pocketsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 10 % | 10 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0052 cm/cm | 0.0052 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 71 | 71 | ASTM D2240 |
| Tensile Strength at Break | 50.3 MPa | 7300 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 2.40 GPa | 348 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Temperature 23.0 °C |
0.700 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 0.339 J | 0.250 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 305 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 - 221 °C | 380 - 430 °F | |
| Middle Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Front Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Nozzle Temperature | 210 - 221 °C | 410 - 430 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Pau Tai UNISTAB LCZ-340 Liquid Stabilizer for Paste Resin
- DuPont™ Biomax® 800C Hydro/Biodegradable Polyester (discontinued **)
- Polymer Resources NY66-IM1-[color]-H Nylon 66, Medium Impact Modified, Heat Stabilized
- Overview of materials for Polyetherimide (PEI), Carbon Fiber Filled
- Eagle Brass 200/201 Nickel Alloy, Annealed
- Braskem H 103 Injection Molding Polypropylene
- Carlson C 800 Nickel-Iron-Chromium Alloy
- Americas Styrenics EB6755 High Impact Polystyrene
- Teknor Apex Monprene® MP-2890M Thermoplastic Elastomer
Copyright © lookpolymers.com All Rights Reserved