- RheTech Products FT7013-721UV Thermoplastic Polyolefin, UV Stabilized, XDV Dark Slate
RheTech Products FT7013-721UV Thermoplastic Polyolefin, UV Stabilized, XDV Dark Slate
| Category | Polymer , Thermoplastic , Polyolefin |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products FT7013-721UV Thermoplastic Polyolefin, UV Stabilized, XDV Dark Slate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Scuff platesLift gate coversI/P componentsClose-out panelsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 28 % | 28 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 61 | 61 | ASTM D2240 |
| Tensile Strength at Break | 17.2 MPa | 2500 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.59 GPa | 230 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm @Temperature 23.0 °C |
4.00 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 18.0 J | 13.3 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 96.7 °C | 206 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.3 °C | 128 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Middle Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Front Barrel Temperature | 216 - 243 °C | 420 - 470 °F | |
| Nozzle Temperature | 221 - 232 °C | 430 - 450 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8320 (UF) Synthetic Oil
- Parker Chomerics Tecknit Consil®-R 856 Pure Silver-Filled Silicone Elastomer
- Fujipoly Industries Sarcon® GR-k Gap Filler Pad
- Isoflon Tisoflon® 6G EXTRA SMOOTH QUALITY Polytetrafluoroethylene & Graphite Coated Glass Fabric
- Solvay TECHNYL® A 218 V35 PA66, 35% glass fiber, DRY
- Dow LDPE 586A Low Density Polyethylene, Packaging Grade
- 3M 12049 Black 3/8" (9.5 mm) Polyurethane Foam
- BASF Elastollan SP 9213 TPUR