RheTech Products FT4900-745UV Thermoplastic Polyolefin, UV Stabilized, CJM Medium Khaki Solid
| Category | Polymer , Thermoplastic , Polyolefin |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products FT4900-745UV Thermoplastic Polyolefin, UV Stabilized, CJM Medium Khaki Solid.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Exterior componentsBodyside moldingsStep padsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 8 % | 8 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM D955 |
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 64 | 64 | ASTM D2240 |
| Tensile Strength at Break | 18.6 MPa | 2700 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.10 GPa | 160 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm @Temperature 23.0 °C |
15.0 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 24.8 J | 18.3 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.6 °C | 195 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.7 °C | 134 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 - 221 °C | 380 - 430 °F | |
| Middle Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Front Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Nozzle Temperature | 210 - 221 °C | 410 - 430 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Raschig Group 2557 AMC Polyester
- Indium Corp. Indalloy 532 Tin Solder Alloy
- Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 4000 hours
- Shin-Etsu Silicones 561P Fluid
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Plasticizer SC
- CoorsTek Zirconia-Toughened Alumina, ZTA
- Entec Hypro™ PP-CP20/2 Impact Copolymer, 20 Melt Flow
- Colorite Polymers 8302 General Purpose Vinyl Compound
- BASF Ultramid® B3ZG6 30% Glass Filled PA6 (Dry)
- Sumitomo Bakelite North America RX® 647 Fiberglass Reinforced Phenolic
Copyright © lookpolymers.com All Rights Reserved