- RheTech Products FT4702-715UV Thermoplastic Polyolefin, UV Stabilized, ZSP Deep Grey
RheTech Products FT4702-715UV Thermoplastic Polyolefin, UV Stabilized, ZSP Deep Grey
| Category | Polymer , Thermoplastic , Polyolefin |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products FT4702-715UV Thermoplastic Polyolefin, UV Stabilized, ZSP Deep Grey.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Exterior componentsGrillesBumper trimDoor componentsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 13 % | 13 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0102 cm/cm | 0.0102 in/in | ASTM D955 |
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength at Break | 19.3 MPa | 2800 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.31 GPa | 190 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 4.00 J/cm @Temperature 23.0 °C |
7.50 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 20.3 J | 15.0 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.1 °C | 124 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Middle Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Front Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Nozzle Temperature | 216 - 227 °C | 420 - 440 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- RheTech Products F37-01 40% Glass Fiber/Mineral Co-Reinforced Polypropylene, Chemically Coupled, Black
- SABIC Innovative Plastics Lexan® ML7664 PC Copolymer (Asia Pacific)
- DuPont Performance Polymers Zytel® 101 NC010 Nylon 66 (Unverified Data**)
- Lubrizol Advanced Materials PEARLTHANE® 11T92EM Thermoplastic Polyurethane Elastomer
- SABIC Innovative Plastics LNP LUBRICOMP RX05495 PA 66
- Trelleborg Emerson & Cuming Eccobond® 45 Two-Component General Purpose Epoxy Adhesive
- A. Schulman POLYBATCH™ FSU-105-E Concentrate Based In LDPE
- DuPont Teijin Films Mylar® RL31 Polyester Film, 75 Gauge
- Fainplast Compounds Hax™ HF 224/4 Flame Retardant Polyolefin Cable Compound
Copyright © lookpolymers.com All Rights Reserved