Premix Thermoplastics PRE-ELEC® PP 1397 Conductive Thermoplastic Compound

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with Carbon Black Filler
Manufacturer Premix Thermoplastics Inc.
Trade Name PRE-ELEC®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® PP 1397 Conductive Thermoplastic Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC® PP 1397 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PP 1397 has excellent mechanical properties and is easy to extrude.Applications: Extrusion of corrugated sheet.Processing: PRE-ELEC® PP 1397 compound can be extruded in the machines using normal processing conditions as with polypropylene.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
Physical Properties Metric English Comments
Density 0.980 g/cc
0.0354 lb/in³
Thickness 102 microns
4.00 mil
Linear Mold Shrinkage 0.013 - 0.019 cm/cm
0.013 - 0.019 in/in
ISO 294-4
Melt Flow 1.2 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 1.2 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
6.0 g/10 min

@Load 5.00 kg,
Temperature 230 °C
 6.0 g/10 min

@Load 11.0 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore A 99
99
ISO 868
Hardness, Shore D 74
74
ISO 868
Film Tensile Strength at Yield, MD 23.0 MPa

@Thickness 0.400 mm
 3340 psi

@Thickness 0.0157 in
 ISO 527
Film Tensile Strength at Yield, TD 22.0 MPa

@Thickness 0.400 mm
 3190 psi

@Thickness 0.0157 in
 ISO 527
Film Elongation at Break, MD 500 %

@Thickness 0.400 mm
 500 %

@Thickness 0.0157 in
 ISO 527
Film Elongation at Break, TD 480 %

@Thickness 0.400 mm
 480 %

@Thickness 0.0157 in
 ISO 527
Film Elongation at Yield, MD 17 %

@Thickness 0.400 mm
 17 %

@Thickness 0.0157 in
 ISO 527
Film Elongation at Yield, TD 16 %

@Thickness 0.400 mm
 16 %

@Thickness 0.0157 in
 ISO 527
Flexural Modulus 1.40 GPa
203 ksi
ISO 178
Izod Impact, Notched (ISO) NB

@Thickness 4.00 mm,
Temperature 23.0 °C
 NB

@Thickness 0.157 in,
Temperature 73.4 °F
 ISO 180
NB

@Thickness 4.00 mm,
Temperature -20.0 °C
 NB

@Thickness 0.157 in,
Temperature -4.00 °F
 ISO 180
Izod Impact, Unnotched (ISO) NB

@Thickness 4.00 mm,
Temperature 23.0 °C
 NB

@Thickness 0.157 in,
Temperature 73.4 °F
 ISO 180
NB

@Thickness 4.00 mm,
Temperature -20.0 °C
 NB

@Thickness 0.157 in,
Temperature -4.00 °F
 ISO 180
Charpy Impact Unnotched NB

@Thickness 102 mm,
Temperature 23.0 °C
 NB

@Thickness 4.00 in,
Temperature 73.4 °F
 ISO 179
NB

@Thickness 102 mm,
Temperature -20.0 °C
 NB

@Thickness 4.00 in,
Temperature -4.00 °F
 ISO 179
Charpy Impact, Notched 1.80 J/cm²

@Thickness 102 mm,
Temperature -20.0 °C
 8.57 ft-lb/in²

@Thickness 4.00 in,
Temperature -4.00 °F
 ISO 179
4.50 J/cm²

@Thickness 102 mm,
Temperature 23.0 °C
 21.4 ft-lb/in²

@Thickness 4.00 in,
Temperature 73.4 °F
 ISO 179
Film Tensile Strength at Break, MD 25.0 MPa

@Thickness 0.400 mm
 3630 psi

@Thickness 0.0157 in
 ISO 527
Film Tensile Strength at Break, TD 23.0 MPa

@Thickness 0.400 mm
 3340 psi

@Thickness 0.0157 in
 ISO 527
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
75/Method Bf
Deflection Temperature at 1.8 MPa (264 psi) 53.0 °C
127 °F
75/Method Af
Vicat Softening Point 151 °C
304 °F
ISO 306/A50
Electrical Properties Metric English Comments
Volume Resistivity <= 1000 ohm-cm

@Thickness 0.400 mm
 <= 1000 ohm-cm

@Thickness 0.0157 in
 ISO D-257
Surface Resistance <= 10000 ohm

@Thickness 0.400 mm
 <= 10000 ohm

@Thickness 0.0157 in
 ISO IEC 61340-5-1
Processing Properties Metric English Comments
Zone 1 210 °C
410 °F
Cylinder
230 °C
446 °F
Die
Zone 2 220 °C
428 °F
Cylinder
230 °C
446 °F
Die
Zone 3 220 °C
428 °F
Die
220 °C
428 °F
Cylinder
Zone 4 230 °C
446 °F
Die
230 °C
446 °F
Cylinder
Zone 5 230 °C
446 °F
Die
230 °C
446 °F
Cylinder
Roll Temperature 60.0 °C
140 °F
3rd Roll
80.0 °C
176 °F
2nd Roll
90.0 °C
194 °F
1st Roll
Drying Temperature 60.0 - 80.0 °C
140 - 176 °F
Pre-drying
Dry Time 2 - 4 hour
2 - 4 hour
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions