Polymer Resources PPX-FR3 Modified-PPO, V-1 Flame Retardant

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Heat Resistant
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX-FR3 Modified-PPO, V-1 Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Modified-Polyphenylene Oxide, V-1 Flame Retardant, 265F HDTFeatures: • Bromine Free • Chlorine FreeProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 4.0 - 9.0 g/10 min

@Load 11.6 kg,
Temperature 250 °C
 4.0 - 9.0 g/10 min

@Load 25.6 lb,
Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 62.1 MPa
9000 psi
ASTM D638
Tensile Strength, Yield 64.1 MPa
9300 psi
ASTM D638
Elongation at Break 25 %
25 %
ASTM D638
Elongation at Yield 5.0 %
5.0 %
ASTM D638
Flexural Strength 89.6 MPa
13000 psi
ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Izod Impact, Notched 1.07 J/cm

@Temperature -30.0 °C
 2.00 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
2.14 J/cm

@Temperature 22.8 °C
 4.00 ft-lb/in

@Temperature 73.0 °F
 ASTM D256
Charpy Impact, Notched 1.47 J/cm²

@Temperature 22.8 °C
 7.00 ft-lb/in²

@Temperature 73.0 °F
 ISO 179/1eA
Gardner Impact 16.9 J
12.5 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 129 °C
265 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648
Vicat Softening Point 135 °C
275 °F
120°C/h, 50 N; ASTM D1525
UL RTI, Electrical 65.0 °C

@Thickness 0.749 mm
 149 °F

@Thickness 0.0295 in
 UL 746
110 °C

@Thickness 1.50 mm
 230 °F

@Thickness 0.0591 in
 UL 746
110 °C

@Thickness 1.70 mm
 230 °F

@Thickness 0.0669 in
 UL 746
110 °C

@Thickness 3.00 mm
 230 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.749 mm
 149 °F

@Thickness 0.0295 in
 UL 746
110 °C

@Thickness 1.50 mm
 230 °F

@Thickness 0.0591 in
 UL 746
110 °C

@Thickness 1.70 mm
 230 °F

@Thickness 0.0669 in
 UL 746
110 °C

@Thickness 3.00 mm
 230 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.749 mm
 149 °F

@Thickness 0.0295 in
 UL 746
105 °C

@Thickness 1.50 mm
 221 °F

@Thickness 0.0591 in
 UL 746
105 °C

@Thickness 1.70 mm
 221 °F

@Thickness 0.0669 in
 UL 746
105 °C

@Thickness 3.00 mm
 221 °F

@Thickness 0.118 in
 UL 746
Flammability, UL94 V-1

@Thickness 1.50 mm
 V-1

@Thickness 0.0591 in
V-1

@Thickness 3.00 mm
 V-1

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D257
Dielectric Strength 24.0 kV/mm
610 kV/in
ASTM D149
Comparative Tracking Index 250 - 400 V
250 - 400 V
UL 746
Hot Wire Ignition, HWI >= 120 sec

@Thickness 1.50 mm
 >= 120 sec

@Thickness 0.0591 in
 UL 746
>= 120 sec

@Thickness 1.70 mm
 >= 120 sec

@Thickness 0.0669 in
 UL 746
>= 120 sec

@Thickness 3.00 mm
 >= 120 sec

@Thickness 0.118 in
 UL 746
High Amp Arc Ignition, HAI 60 - 120 arcs

@Thickness 1.50 mm
 60 - 120 arcs

@Thickness 0.0591 in
 UL 746
60 - 120 arcs

@Thickness 1.70 mm
 60 - 120 arcs

@Thickness 0.0669 in
 UL 746
60 - 120 arcs

@Thickness 3.00 mm
 60 - 120 arcs

@Thickness 0.118 in
 UL 746
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 249 - 299 °C
480 - 570 °F
Middle Barrel Temperature 260 - 304 °C
500 - 580 °F
Front Barrel Temperature 271 - 310 °C
520 - 590 °F
Melt Temperature 288 - 316 °C
550 - 600 °F
Mold Temperature 71.1 - 98.9 °C
160 - 210 °F
Drying Temperature 104 - 110 °C
220 - 230 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.001