Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 250 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648
Nylene® Norpex® AX10GF , 10% Glass Reinforced Polyphenylene Ether
Description: Norpex® AX10GF is a 10% glass fiber reinforced Polyphenylene Ether. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric..
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648
Quadrant EPP Techtron® 1000 PPS Extruded Polyphenylene Sulfide (ASTM Product Data Sheet)
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648
Polymer Resources PPX-FR3 Modified-PPO, V-1 Flame Retardant
Modified-Polyphenylene Oxide, V-1 Flame Retardant, 265F HDTFeatures: • Bromine Free • Chlorine FreeProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-..
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648
Polymer Resources PPX-GP1-[color]-EN Modified-PPO, Extrusion Grade
Modified-Polyphenylene Oxide, Extrusion Grade, 265F HDTFeatures: • Hydrolytically Stable • Low to No Water AbsorptionProcess: Extrusion Notes: All physical, mechanical and thermal testing conduc..
Deflection Temperature at 1.8 MPa (264 psi) 121 °C

@Thickness 3.20 mm
250 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics Lexan® FXE1112T PC Copolymer (Europe-Africa-Middle East)
Lexan* FXE1112T Lexan* polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers good low temperature (-20 C) ductility in combination with high flow ch..
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
SABIC Innovative Plastics Lexan® HF1110 PC (Europe-Africa-Middle East)
LEXAN HF1110 is a high flow grade especially designed for applications that require thin wall sections and high flow lengths.
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
SABIC Innovative Plastics Lexan® HPS1R PC (Asia Pacific)
High flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, e-beam and gamma sterilizable. Contains..
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
SABIC Innovative Plastics Lexan® OQ1022 PC
Standard Flow OQ Resin
Deflection Temperature at 1.8 MPa (264 psi) 121 °C

@Thickness 3.20 mm
250 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics Lexan® FXG1414T PC Copolymer (Asia Pacific)
PC-siloxane copolymer in special ""Diamond Sparkle"" colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Unannealed, 0.125 in bars; ASTM D648
PolyOne Lubri-Tech™ ATH-000/5M Acetal-Homopolymer  (discontinued **)
Description/Features:Molybdenum Disulfide LubricatedInformation provided by PolyOne Corporation.
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
SABIC Innovative Plastics Lexan® HF1140 PC (Europe-Africa-Middle East)
Ideal for disposables/short life cycles. Good clarity, heat resistance, property retention and dimensional stability. FDA food contact compliant in limited colors.Effective January 15th, 2007 this..
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
SABIC Innovative Plastics Lexan® HP1R PC
High flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO sterilizable. Contains a higher amount..
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
SABIC Innovative Plastics Lexan® LUX9132C PC COPOLYMER
Lexan* LUX9132C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and..
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
SABIC Innovative Plastics Lexan® ML3982 PC (Europe-Africa-Middle East)
LEXAN ML3982 is an UV stabilized grade, with an excellent flow. It contains a release agent to ensure easy processing.
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Saint-Gobain Rulon® E Grade Bearing/Seal PTFE  (discontinued **)
Rulon® is the Saint-Gobain trade name for their family of proprietary PTFE compounds. This family of materials offers the combination of high compressive strength, low coefficient of friction, and ..
Deflection Temperature at 1.8 MPa (264 psi) >= 121 °C

@Thickness 6.40 mm
>= 250 °F

@Thickness 0.252 in
Unannealed; ASTM D648
LG Chemical LUPOY GN1002FH PC, Halogen Free, Flame Retardant, Heat Resistant
Description: Injection Molding, PC, Halogen Free Flame Retardant, Heat Resistant, Chemical Resistance, High ImpactApplication: IT/OA Housing and Components (Adaptor)CAS: 103598-77-2, 25232-40-0 and ..
Deflection Temperature at 1.8 MPa (264 psi) 121 °C

@Thickness 3.20 mm
250 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP ZX05506 PPE+PS (Asia Pacific)
LNP LUBRICOMP* ZX05506 is a compound based on PPE+PS Blend resin containing Graphite Powder, PTFE. Added features of this material include: Internally Lubricated.
Deflection Temperature at 1.8 MPa (264 psi) 121 °C

@Thickness 3.20 mm
250 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRILOY Z2000 PPO
LNP* LUBRILOY* Z2000 is a compound based on PPO resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Unannealed; ASTM D648
Techmer ES HiFill® HDPE E GF15 15% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightProcessing Method: ExtrusionInformation provided by TP Composites, Inc.
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Unannealed; ASTM D648
Techmer ES HiFill® HDPE GF15 50100 15% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightProcessing Method: ExtrusionInformation provided by TP Composites, Inc.
Deflection Temperature at 1.8 MPa (264 psi) 121 °C

@Thickness 6.40 mm
250 °F

@Thickness 0.252 in
ASTM D648
Samsung Cheil Industries Infino® GW-1041 PC/ABS, Unreinforced Recycled
Eco-friendly Post-Consumer recycled content.Information provided by Samsung Cheil Industries.
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Unannealed; ISO 75-2/A
Styron CALIBREâ„¢ 320 UV Polycarbonate Resin
Overview: CALIBREâ„¢ 302 UV polycarbonate resin contains a proprietary UV stabilization package that combines industry standard stabilization against ultraviolet radiation with low plate-out and ..
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
0.157 in, unannealed; ASTM D648
Styron EMERGEâ„¢ 4530-15 Polycarbonate
EMERGEâ„¢ PC 4530-15 advanced resin is a general purpose polycarbonate resin offering ultraviolet light stability, ignition resistance, heat resistance and excellent toughness. Applications: Co..
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648
Westlake Plastics Propylux® CN-F Polypropylene (conductive)
Non-sloughing, carbon-fiber-filled material with good chemical resistance, and high strength and stiffness and good temperature resistance to 215F. This material is light weight, easily machined an..
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648
Clariant PA213M40 Nylon 6, 40% Mineral Reinforced, Heat Stabilized
Data provided by Clariant Masterbatches
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648
A. Schulman ComAlloy Hiloy® 261 Glass Reinforced, Modified SMA
Data provided by the manufacturer, ComAlloy International Company.10% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 1.8 MPa (264 psi) 121 - 152 °C
250 - 306 °F
Average value: 140 °C Grade Count:73
Overview of materials for Polycarbonate, Glass + PTFE Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Glass + PTFE Filled". Each property range of values reported is minimum and maximum value..
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Lexan® SLX2071T PC Copolymer (Europe-Africa-Middle East)
High viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colors
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648
Polymer Resources PPX-FR7 Modified PPO, V-0 Flame Retardant, Medium Heat, 250 HDT  (Unverified Data**)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.