ExxonMobil LDPE LD 100.BW Low Density Polyethylene Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Exxon Chemical
Trade Name	LDPE
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LDPE LD 100.BW Low Density Polyethylene Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LD 100.BW is a LDPE grade, offering a good balance of optical and mechanical properties. Several additive packages are available according to the required surface properties.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: No Thermal Stabilizer: YesApplications: Blend PartnerCast FilmCompoundingFoamsForm Fill and Seal PackagingFreezer FilmLamination FilmLight Duty Shrink FilmLinersMail BagProduce BagsShoppersTextile PackagingTough Medium Sized Molding Information provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.923 g/cc	0.0333 lb/in³	ExxonMobil method
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 190 °C	2.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	11.0 MPa	1600 psi	ASTM D882
Film Tensile Strength at Yield, TD	11.0 MPa	1600 psi	ASTM D882
Film Elongation at Break, MD	330 %	330 %	ASTM D882
Film Elongation at Break, TD	550 %	550 %	ASTM D882
Elmendorf Tear Strength MD	150 g	150 g	ASTM D1922
Elmendorf Tear Strength TD	120 g	120 g	ASTM D1922
Dart Drop Test	80.0 g	0.176 lb	ASTM D1709A
Film Tensile Strength at Break, MD	24.8 MPa	3600 psi	ASTM D882
Film Tensile Strength at Break, TD	22.1 MPa	3200 psi	ASTM D882
1% Secant Modulus, MD	207 MPa	30000 psi	ASTM D882
1% Secant Modulus, TD	228 MPa	33000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 230 °C	<= 446 °F	Peak Melting Point; ExxonMobil method

Optical Properties	Metric	English	Comments
Haze	6.1 %	6.1 %	ASTM D1003
Gloss	63 %	63 %	45°; ASTM D2457