Polymer Resources PC-UV1-D-[color]-1 Polycarbonate, UV-stabilized, Low Flow with Mold Release

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PC-UV1-D-[color]-1 Polycarbonate, UV-stabilized, Low Flow with Mold Release.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polycarbonate, UV-stabilized, Low Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 5.0 - 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
5.0 - 10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 70
70
ASTM D785
Hardness, Rockwell R 118
118
ASTM D785
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D638
Tensile Strength, Yield 62.1 MPa
9000 psi
ASTM D638
Elongation at Break 130 %
130 %
ASTM D638
Elongation at Yield 7.0 %
7.0 %
ASTM D638
Flexural Strength 96.5 MPa
14000 psi
ASTM D790
Flexural Modulus 2.31 GPa
335 ksi
ASTM D790
Izod Impact, Notched 9.08 J/cm

@Temperature 22.8 °C
17.0 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Gardner Impact 36.2 J
26.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 138 °C
280 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 132 °C
270 °F
ASTM D648
Vicat Softening Point 154 °C
310 °F
120°C/h, 50 N; ASTM D1525
UL RTI, Electrical 120 °C

@Thickness 1.50 mm
248 °F

@Thickness 0.0591 in
UL 746
120 °C

@Thickness 3.00 mm
248 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 120 °C

@Thickness 1.50 mm
248 °F

@Thickness 0.0591 in
UL 746
120 °C

@Thickness 3.00 mm
248 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 105 °C

@Thickness 1.50 mm
221 °F

@Thickness 0.0591 in
UL 746
110 °C

@Thickness 3.00 mm
230 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 V-2

@Thickness 1.50 mm
V-2

@Thickness 0.0591 in
V-2

@Thickness 3.00 mm
V-2

@Thickness 0.118 in
Optical Properties Metric English Comments
Haze 1.0 %
1.0 %
ASTM D1003
UV Transmittance 88 %
88 %
ASTM D1003
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Strength 11.8 kV/mm
300 kV/in
ASTM D149
Comparative Tracking Index 175 - 250 V
175 - 250 V
UL 746
Hot Wire Ignition, HWI 30 - 60 sec

@Thickness 1.50 mm
30 - 60 sec

@Thickness 0.0591 in
UL 746
30 - 60 sec

@Thickness 3.00 mm
30 - 60 sec

@Thickness 0.118 in
UL 746
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 1.50 mm
>= 120 arcs

@Thickness 0.0591 in
UL 746
>= 120 arcs

@Thickness 3.00 mm
>= 120 arcs

@Thickness 0.118 in
UL 746
High Voltage Arc-Tracking Rate, HVTR 25.4 - 80.0 mm/min
1.00 - 3.15 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 288 - 310 °C
550 - 590 °F
Middle Barrel Temperature 299 - 321 °C
570 - 610 °F
Front Barrel Temperature 310 - 332 °C
590 - 630 °F
Melt Temperature 316 - 343 °C
600 - 650 °F
Mold Temperature 82.2 - 116 °C
180 - 240 °F
Drying Temperature 118 - 124 °C
245 - 255 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Outdoor Suitability f1
Vent 0.0005