Polymer Property : Melt Flow = 10 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most.

Physical Properties	Metric	English	Comments
Melt Flow	7.0 - 10 g/10 min @Load 2.16 kg, Temperature 230 °C	7.0 - 10 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238/L
NIZHNEKAMSKNEFTEKHIM PP 4310M (EP1X30F) Propylene and Ethylene Copolymer Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation r..
Melt Flow	7.0 - 10 g/10 min @Load 2.16 kg, Temperature 230 °C	7.0 - 10 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238/L
NIZHNEKAMSKNEFTEKHIM PP 4316M (EP1X35AF) Propylene and Ethylene Copolymer Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation r..
Melt Flow	5.0 - 10 g/10 min @Load 2.16 kg, Temperature 265 °C	5.0 - 10 g/10 min @Load 4.76 lb, Temperature 509 °F	ASTM D1238
Polymer Resources PC/TP-GP2-G20 PC/Polyester Alloy, 20% Glass Reinforced Excellent Chemical Resistance, 20% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information p..
Melt Flow	5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C	5.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
Polymer Resources PC-FR1A-D Polycarbonate, Flame Retardant, Low Flow Polycarbonate, Flame Retardant, Low FlowFeatures: • High Impact Resistance • High Viscosity • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing co..
Melt Flow	5.0 - 10 g/10 min	5.0 - 10 g/10 min	ASTM D1238
Polymer Resources PC-FR-IM1 Polycarbonate, Preliminary Data Sheet, Low Temperature Impact and Flame Retardant Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Melt Flow	4.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C	4.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
Polymer Resources PC-G20-[color]-1 Polycarbonate, 20% Glass Reinforced with Mold Release Polycarbonate, 20% Glass Reinforced with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information..
Melt Flow	5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C	5.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
Polymer Resources PC-GP1-D-[color]-6 Polycarbonate, FDA-compliant Feedstocks, Low Flow with Mold Release Polycarbonate, FDA-compliant Feedstocks, Low Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sampl..
Melt Flow	2.0 - 10 g/10 min @Load 11.6 kg, Temperature 250 °C	2.0 - 10 g/10 min @Load 25.6 lb, Temperature 482 °F	ASTM D1238
Polymer Resources PPX-G5 Modified-PPO, 5% Glass Reinforced Modified-Polyphenylene Oxide, 5% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pro..
Melt Flow	6.0 - 10 g/10 min @Load 11.6 kg, Temperature 250 °C	6.0 - 10 g/10 min @Load 25.6 lb, Temperature 482 °F	ASTM D1238
Polymer Resources PPX-GP2 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 250F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati..
Melt Flow	1.0 - 10 g/10 min @Load 5.00 kg, Temperature 250 °C	1.0 - 10 g/10 min @Load 11.0 lb, Temperature 482 °F	ASTM D1238
Polymer Resources PC/ABS-G30 General Purpose PC/ABS Alloy, 30% Glass Filled PC/ABS Alloy, General Purpose, 30% Glass FilledProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provi..
Melt Flow	5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C	5.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
Polymer Resources PC-FD1 Polycarbonate, FDA-compliant Feedstocks, Low Flow, Gamma Resistant Polycarbonate, FDA-compliant Feedstocks, Low Flow, Gamma ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sample..
Melt Flow	8.0 - 10 g/10 min @Load 3.80 kg	8.0 - 10 g/10 min @Load 8.38 lb
Solvay Specialty Polymers Hylar® MP10 PVDF Polyvinylidene Fluoride  (discontinued **) Data provided by the manufacturer.Hylar® polymers have the characteristic stability of fluoropolymers combined with a unique polarity that influences its solubility and electrical properties. In a..
Melt Flow	7.0 - 10 g/10 min	7.0 - 10 g/10 min	ASTM D1238
Kolon KOCETALÂ® LF302 Wear Modified Acetal Resin Improved wear property and dimensional stability. Applications: Products for low noise and precision gear. Information provided by API-Kolon.
Melt Flow	8.0 - 10 g/10 min @Load 5.00 kg, Temperature 200 Â°C	8.0 - 10 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ASTM D1238
Lavergne VYSTYRENE PS 3904 High Impact Polystyrene Vystyrene PS 3904 is a black impact modified polystyrene compound with balanced impact/stiffness properties designed for injection molding applicationsFeatures: -High resilience -Excellent process..
Melt Flow	7.0 - 10 g/10 min @Load 2.16 kg, Temperature 190 Â°C	7.0 - 10 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238-00
Ipiranga Petrochem PRA 0852 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr..
Melt Flow	3.6 - 10 g/10 min	3.6 - 10 g/10 min
Shandong Dongyue Shenzhou New Material Co DS603B Fluorinated Ethylene Propylene Dispersion (DS603A/B) Conformable with: Q/DYS 004-2007Fluorinated Ethylene Propylene concentrated dispersion is the copolymer of TFE and HFP, stabilized with non-ionic surfactant. It endow FEP products which can't be pr..
Melt Flow	6.0 - 10 g/10 min	6.0 - 10 g/10 min	ASTM D1238
Shuman SP810 Black Polystyrene High Impact Good impact strength, easy processability, good surface appearance, ULInformation provided by Shuman Plastics, Inc.
Melt Flow	6.0 - 10 g/10 min	6.0 - 10 g/10 min	ASTM D1238
Shuman SP880 Grey Polystyrene High Impact Good impact strength, easy processability, good surface appearance, ULInformation provided by Shuman Plastics, Inc.
Melt Flow	5.0 - 10 g/10 min @Temperature 230 °C	5.0 - 10 g/10 min @Temperature 446 °F	Condition L; ASTM D1238
A. Schulman POLYFORT™ FPP 1285 Glass Fiber-Reinforced Copolymer Polypropylene DescriptionPolyfort® FPP1285 is a 20% glass fiber-reinforced copolymer polypropylene.Information provided by A. Schulman.
Melt Flow	7.0 - 10 g/10 min @Temperature 230 °C	7.0 - 10 g/10 min @Temperature 446 °F	ASTM D1238
A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 2122UV-M-31 is a black 40% talc filled polypropylene. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman.
Melt Flow	7.0 - 10 g/10 min @Temperature 230 °C	7.0 - 10 g/10 min @Temperature 446 °F	ASTM D1238
A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 2122UV-M-31 is a black 40% talc filled polypropylene. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman.
Melt Flow	7.0 - 10 g/10 min @Temperature 230 °C	7.0 - 10 g/10 min @Temperature 446 °F	Condition L; ASTM D1238
A. Schulman POLYFORT™ FPP 2388 Glass Reinforced Polypropylene DescriptionPolyfort® FPP 2388 is a 5% glass reinforced polypropylene.Information provided by A. Schulman.
Melt Flow	6.0 - 10 g/10 min @Temperature 230 °C	6.0 - 10 g/10 min @Temperature 446 °F	ASTM D1238
A. Schulman PP 1259 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 1259 is a medium impact polypropylene with easier molding characteristics for thinner parts and longer flow distances. Lower molding pressures and heats often reduce war..
Melt Flow	6.0 - 10 g/10 min @Temperature 230 °C	6.0 - 10 g/10 min @Temperature 446 °F	ASTM D1238
A. Schulman PP 1259 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 1259 is a medium impact polypropylene with easier molding characteristics for thinner parts and longer flow distances. Lower molding pressures and heats often reduce war..
Melt Flow	5.0 - 10 g/10 min @Temperature 230 °C	5.0 - 10 g/10 min @Temperature 446 °F	Condition L; ASTM D1238
A. Schulman POLYFORT™ FPP 1285 Glass Fiber-Reinforced Copolymer Polypropylene DescriptionPolyfort® FPP1285 is a 20% glass fiber-reinforced copolymer polypropylene.Information provided by A. Schulman.
Melt Flow	9.0 - 10 g/10 min @Load 2.16 kg, Temperature 230 °C	9.0 - 10 g/10 min @Load 4.76 lb, Temperature 446 °F
Breplast Bretene PP Polypropylene Composite Recovered polypropylene compositeInformation provided by Breplast S.p.A.
Melt Flow	7.0 - 10 g/10 min @Load 12.5 kg	7.0 - 10 g/10 min @Load 27.6 lb
Solvay Specialty Polymers Hylar® MP20 PVDF Polyvinylidene Fluoride  (discontinued **) Data provided by the manufacturer.Hylar® polymers have the characteristic stability of fluoropolymers combined with a unique polarity that influences its solubility and electrical properties. In a..
Melt Flow	6.0 - 10 g/10 min @Load 2.16 kg, Temperature 230 °C	6.0 - 10 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Samyang Triel® 5206SP Thermoplastics Polyetherester Elastomer, Double Extrusion Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5206SP is intended for double extrusion.Information provided by Samyang.
Melt Flow	7.0 - 10 g/10 min @Temperature 230 °C	7.0 - 10 g/10 min @Temperature 446 °F	Condition L; ASTM D1238
A. Schulman POLYFORT™ FPP 2388 Glass Reinforced Polypropylene DescriptionPolyfort® FPP 2388 is a 5% glass reinforced polypropylene.Information provided by A. Schulman.