- Polymer Property : Melt Flow = 10 g/10 min
Polymer Property : Melt Flow = 10 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 2.0 - 10 g/10 min @Load 2.16 kg, Temperature 265 °C |
2.0 - 10 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| Polymer Resources PC/TP-GP2-G10 PC/Polyester Alloy, 10% Glass Reinforced Excellent Chemical Resistance, 10% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information p.. |
|||
| Melt Flow | 2.0 - 10 g/10 min @Load 2.16 kg, Temperature 265 °C |
2.0 - 10 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| Polymer Resources PC/TP-GP3-G10 PC/Polyester Alloy, 10% Glass Reinforced Superior Chemical Resistance, 10% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
| Melt Flow | 4.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
4.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-G20 Polycarbonate, 20% Glass Reinforced Polycarbonate, 20% Glass ReinforcedFeatures: • Flame Retardant • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-p.. |
|||
| Melt Flow | 4.0 - 10 g/10 min | 4.0 - 10 g/10 min | ASTM D1238 |
| Polymer Resources PC-G20-[color]-WS Polycarbonate, 20% Glass Reinforced Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Melt Flow | 2.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
2.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-G40 Polycarbonate, 40% Glass Reinforced Polycarbonate, 40% Glass ReinforcedFeatures: • Flame Retardant • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-p.. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-GP1-D-[color]-1 Polycarbonate, General Purpose, Low Flow with Mold Release Polycarbonate, General Purpose, Low Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inform.. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-GP1-D-[color]-5 Polycarbonate, FDA-compliant Feedstocks, Low Flow Polycarbonate, FDA-compliant Feedstocks, Low FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pro.. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-GP1-D-[color]-6 Polycarbonate, FDA-compliant Feedstocks, Low Flow with Mold Release Polycarbonate, FDA-compliant Feedstocks, Low Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sampl.. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-UV1-D Polycarbonate, UV-stabilized, Low Flow Polycarbonate, UV-stabilized, Low FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Po.. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 - 10 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Ineos Nova 602 Crystal Polystyrene GP Grade
(discontinued **) Broad, medium melt flow range, Broad Vicat rangeApplications: Any; Injection Molding and ExtrusionProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise spe.. |
|||
| Melt Flow | 7.0 - 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.0 - 10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238/L |
| NIZHNEKAMSKNEFTEKHIM PP 1500M (X30G) Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
| Melt Flow | 8.0 - 10 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 - 10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| FKuR Kunststoff Bio-Flex® S 6540 Compostable PLA Blend The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any sta.. |
|||
| Melt Flow | 2.0 - 10 g/10 min | 2.0 - 10 g/10 min | (Condition L) ASTM D-1238 |
| Multibase Multi-Flex® TPE A 4710 NAT The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Load 10.0 kg, Temperature 230 °C |
5.0 - 10 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM D1238 |
| Shanghai Ofluorine J-2 PVDF Extrusion Grade Description: J-2 PVDF is a kind of granules homopolymer, which has middle melt viscosity, J-2 is more suitable for extrusion process. J-2 PVDF pellets as raw materials, the finished products has exc.. |
|||
| Melt Flow | 4.0 - 10 g/10 min | 4.0 - 10 g/10 min | ASTM D1238 |
| Shuman 330 White PC/ABS Alloy Good impact strength, easy processability, good surface gloss, good chemical resistance Formerly Shuman 705 ABS/PC AlloyInformation provided by Shuman Plastics, Inc. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | 230/2.16; May be specified; ASTM D1238 |
| Plastics Group Polifil® GFRMPPCC-30 30% Glass Reinforced Polypropylene, High Impact Polifil® GFRMPPCC series compounds are high impact polypropylenes reinforced with chemically coupled glass fibers. This combination provides higher impact strength while retaining high stiffness.Ap.. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | ASTM D1238 |
| A. Schulman POLYFORT™ FPP 1182 Talc Fortified Impact Resistant Polypropylene DescriptionPolyfort® FPP 1182 is a 20% talc fortified impact resistant polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 7.0 - 10 g/10 min @Temperature 230 °C |
7.0 - 10 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman POLYFORT™ FPP 2388 Glass Reinforced Polypropylene DescriptionPolyfort® FPP 2388 is a 5% glass reinforced polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | ISO 1133 |
| Chengdu Polyster CH7563 Thermoplastic Polyether-ester Elastomer (TPEE) Poly-basic block copolymer. Good compatibility with PBT, PET and PA. For blending with PBT, PET and PA to improve impact resilience properties.Information provided by Chengdu Polyster Co., Ltd. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | ISO 1133 |
| Chengdu Polyster FH5550 Thermoplastic Polyether-ester Elastomer (TPEE) Blend of H5550 and self-made flame retardant material. Flame retardant, good balance of low and high temperature properties. Applications requiring flame retardancy, such as wires, cables and optica.. |
|||
| Melt Flow | 8.0 - 10 g/10 min | 8.0 - 10 g/10 min | ISO 1133 |
| Chengdu Polyster H4543 Thermoplastic Polyether-ester Elastomer (TPEE) Low modulus molding and injection grade. Contains improved color- stable antioxidants. Applications requiring high original color retention. Molded and injected products for consumer use, such as se.. |
|||
| Melt Flow | 7.0 - 10 g/10 min | 7.0 - 10 g/10 min | ISO 1133 |
| Chengdu Polyster H7560Y Thermoplastic Polyether-ester Elastomer (TPEE) High modulus molding and extrusion grade. Contains improved color- stable antioxidants. Low frictional coefficient and good abrasion resistance. Spherical socket of ball joint and lock of automobile.. |
|||
| Melt Flow | 7.0 - 10 g/10 min | 7.0 - 10 g/10 min | ISO 1133 |
| Chengdu Polyster H9275Y Thermoplastic Polyether-ester Elastomer (TPEE) High modulus molding and injection grade. Contains improved color- stable antioxidants. Excellent heat-ageing resistance and toughness. Applications requiring high strength, high toughness and good .. |
|||
| Melt Flow | 4.0 - 10 g/10 min @Load 5.00 kg, Temperature 372 °C |
4.0 - 10 g/10 min @Load 11.0 lb, Temperature 702 °F |
|
| Daikin NEOFLON NP-120 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding.Applications: Heavy wall wire insulation, cable jacketing, tubes.. |
|||
| Melt Flow | 3.0 - 10 g/10 min @Load 5.00 kg, Temperature 230 °C |
3.0 - 10 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
| Eurostar Starpylen MFB44S PP, Glass Bead/Glass Fiber Filled Starpylen MFB44S is a Glass Beads, Glass Fiber Reinforced, Polypropylene Injection Molding Resin heat stabilized (also known as Starpylen WS 2020VK S37.7)Information provided by Eurostar. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Load 5.00 kg, Temperature 230 °C |
5.0 - 10 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
| Eurostar Starpylen MZ006S PP, Glass Fiber Filled, Injection Molded Starpylen MZ006S is a Glass fiber Reinforced, Polypropylene Injection Molding Resin heat stabilized (also known as Starpylen WT 30GF S3)Information provided by Eurostar. |
|||
| Melt Flow | 6.0 - 10 g/10 min | 6.0 - 10 g/10 min | ASTM D1238 |
| Buckeye Polymers BP HDPE 9610 R RLK High Density Polyethylene Product Information: Our HDPE grade of materials are designed to offer excellent physical properties while providing cost savings versus higher cost prime equivalents. Buckeye Polymers HDPE materia.. |
|||
| Melt Flow | 3.0 - 10 g/10 min | 3.0 - 10 g/10 min | ASTM D1238 |
| Polymer Resources PPX-MF-FR3 Modified PPO, UL 94 V-0 with HDT of 230 F, Mineral Reinforced
(Unverified Da Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | ASTM D1238 |
| Aaron Industries AAROPRENE® GFABS 4010 Glass Filled Acrylonitrile-Butadiene Styrene AAROPRENE® GFABS 4000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Melt Flow | 8.0 - 10 g/10 min | 8.0 - 10 g/10 min | |
| Ashley Polymers Ashlene® R190H Acetal General purpose, reprocessed copolymer, excellent toughness, strength, stiffness and lubricity. UV stabilized for good weatherability. Available in Natural and Black. Natural: Designated R190H-N3.. |
|||