Ineos Barex® 218 E Acrylonitrile-Methyl Acrylate Copolymer
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylic (PMMA) , Acrylonitrile-Methyl Acrylate Copolymer |
| Manufacturer | Ineos Olefins & Polymers USA |
| Trade Name | Barex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Barex® 218 E Acrylonitrile-Methyl Acrylate Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Extrusion Grade. Barex® Resins are available in either natural or blue tint. Barex® 218E is most commonly used for thermoformed sheet applications in which high impact performance is required.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | |
| Apparent Bulk Density | 0.680 g/cc | 0.0246 lb/in³ | |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | ASTM D955 |
| Melt Flow | 3.0 g/10 min @Load 12.5 kg, Temperature 200 °C |
3.0 g/10 min @Load 27.6 lb, Temperature 392 °F |
2 mm x 8 mm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 45 | 45 | |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | |
| Elongation at Break | 4.0 % | 4.0 % | |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | |
| Flexural Modulus | 2.70 GPa | 392 ksi | |
| Izod Impact, Notched | 9.00 J/cm | 16.9 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.30 J/g-°C | 0.311 BTU/lb-°F | |
| Thermal Conductivity | 0.260 W/m-K | 1.80 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ASTM D648 |
| Vicat Softening Point | 77.0 °C | 171 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F |
Users viewing this material also viewed the following:
- MV Labs RH450 (NH4)3RhCl6 Ammonium hexachlororhodate(III)
- PSM Industries Pacific Sintered Metals Iron F-241-S1 Powdered Metal
- NOVA Chemicals Novapol® LF-Y320-C Fractional Melt LDPE Film Resin
- SABIC Innovative Plastics Lexan® HFD1930 PC Copolymer (Europe-Africa-Middle East)
- Nye Lubricants 774VL (NG) Synthetic Oil
- Mallard Creek Polymers Rovene® 4301 Styrene-Butadiene Emulsion
- Covestro Bayfill® 312 Polyurethane Semi-Rigid Foam, MDI-based 2-Component Liquid System
- Entec Hypro™ PP-CP20/2 Impact Copolymer, 20 Melt Flow
Copyright © lookpolymers.com All Rights Reserved