Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | With Flow; ISO 2577 |
0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | Across Flow; ISO 2577 | |
Melt Index of Compound | 18 g/10 min @Load 5.00 kg, Temperature 230 °C |
18 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | <= 48.0 MPa | <= 6960 psi | ISO/R527 |
Elongation at Yield | 6.0 % | 6.0 % | ISO/R527 |
Flexural Strength | <= 80.0 MPa | <= 11600 psi | ISO 178 |
Flexural Modulus | 2.60 GPa @Temperature 23.0 °C |
377 ksi @Temperature 73.4 °F |
ISO 178 |
Charpy Impact, Notched | 0.700 J/cm² @Temperature -20.0 °C |
3.33 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | 120°C/h; ISO 75/1 |
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | 120°C/h; ISO 75/1 |
Vicat Softening Point | 100 °C @Load 5.001 kg |
212 °F @Load 11.03 lb |
50°C/h; ISO 306 |
109 °C @Load 1.00 kg |
228 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Melt Temperature | 190 - 230 °C | 374 - 446 °F | |
Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
Drying Temperature | 80.0 °C | 176 °F | |
Dry Time | 2 - 4 hour | 2 - 4 hour | in circulation dryer |
2 - 4 hour | 2 - 4 hour | in fresh-air dryer | |
2 - 4 hour | 2 - 4 hour | in desiccant air dryer | |
Injection Pressure | 90.0 - 150 MPa | 13100 - 21800 psi | |
Back Pressure | 1.00 - 1.50 MPa | 145 - 218 psi |
Descriptive Properties | Value | Comments |
---|---|---|
Holding Pressure () | 20-40 | % of injection pressure |
Injection Speed () | High |