PTS Tristar® PC-10FRN (V) 15 MFI, 5VA, Flame Retardant, UV Stabilized Polycarbonate With Release
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Tristar® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Tristar® PC-10FRN (V) 15 MFI, 5VA, Flame Retardant, UV Stabilized Polycarbonate With Release.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ROHS Compliant.Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Water Absorption | 0.18 % | 0.18 % | 24 hours at 73°F; ASTM D570 |
| Melt Flow | 15 g/10 min @Load 1.20 kg, Temperature 300 °C |
15 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 58.6 MPa @Thickness 3.17 mm |
8500 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 75 % @Thickness 3.17 mm |
75 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Yield Strength | 86.2 MPa @Thickness 3.17 mm |
12500 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 2.14 GPa @Thickness 3.17 mm |
310 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 5.87 J/cm @Thickness 3.17 mm |
11.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Tensile Impact Strength | 443 kJ/m² @Thickness 3.17 mm |
211 ft-lb/in² @Thickness 0.125 in |
ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.2 µm/m-°C @Temperature -40.0 - 95.0 °C |
39.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E831-06 |
| CTE, linear, Transverse to Flow | 68.4 µm/m-°C @Temperature -40.0 - 95.0 °C |
38.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E831-06 |
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C | 265 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 134 °C | 273 °F | ISO 75 |
| UL RTI, Electrical | 125 °C | 257 °F | |
| UL RTI, Mechanical with Impact | 115 °C | 239 °F | |
| UL RTI, Mechanical without Impact | 125 °C | 257 °F | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| 5VA @Thickness 2.50 mm |
5VA @Thickness 0.0984 in |
Black, Gray, Beige | |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
||
| Oxygen Index | 37.6 % | 37.6 % | ASTM D2863 |
| Glow Wire Test | 775 °C | 1430 °F | GWIT |
| 960 °C | 1760 °F | GWFI |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 3.00e+15 ohm-cm | 3.00e+15 ohm-cm | 96 hours at 90°C, 50% RH; ASTM D257 |
| 6.00e+15 ohm-cm | 6.00e+15 ohm-cm | 40 hours at 23°C, 50% RH; ASTM D257 | |
| Dielectric Strength | 24.0 kV/mm @Thickness 3.17 mm |
610 kV/in @Thickness 0.125 in |
ASTM D149 |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | PLC 6 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | PLC 2 |
| Hot Wire Ignition, HWI | 15 - 30 sec @Thickness 1.50 mm |
15 - 30 sec @Thickness 0.0591 in |
PLC 3 |
| 15 - 30 sec @Thickness 2.50 mm |
15 - 30 sec @Thickness 0.0984 in |
PLC 3 | |
| 30 - 60 sec @Thickness 3.00 mm |
30 - 60 sec @Thickness 0.118 in |
PLC 2 | |
| High Amp Arc Ignition, HAI | 60 - 120 arcs @Thickness 2.50 mm |
60 - 120 arcs @Thickness 0.0984 in |
PLC 1 |
| 60 - 120 arcs @Thickness 3.00 mm |
60 - 120 arcs @Thickness 0.118 in |
PLC 1 | |
| >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
PLC 0 | |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | PLC 3 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 254 - 274 °C | 490 - 525 °F | |
| Middle Barrel Temperature | 266 - 277 °C | 510 - 530 °F | |
| Front Barrel Temperature | 277 - 293 °C | 530 - 560 °F | |
| Nozzle Temperature | 271 - 293 °C | 520 - 560 °F | |
| Melt Temperature | 282 - 304 °C | 540 - 580 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 75.8 - 124 MPa | 11000 - 18000 psi | |
| Back Pressure | 0.345 - 1.38 MPa | 50.0 - 200 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Edge Gate | Slow to Medium | |
| Tab Gate | Medium to Fast | |
| Tunnel Gate | Fast |
Users viewing this material also viewed the following:
- Nylene® 321 (HS) Impact Modified Nylon 6
- Solvay Specialty Polymers Amodel® FR-4133 Polyphthalamide (PPA) Resin, 33% Glass Reinforced, at 50% RH (disco
- Iran Petrochemical (PCC) 5218EA High Density Polyethylene
- Karina E 800-35/1-Y-CRB Ivory PVC Compound
- Ineos N20N-00 Polypropylene Impact Copolymer
- SABIC Innovative Plastics ULTEM 2100 PEI
- Unifrax Fiberfrax® Washed 757 High Purity High-Index Fiber
- A. Schulman ComAlloy® E-14756 Flame Retardant Easy Flow Polycarbonate Alloy
- Eurostar Starflam BFR460B1 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
- Unifrax Fiberfrax® Bulk 8000 AZS High-Temperature Fiber
Copyright © lookpolymers.com All Rights Reserved