- Styrene Acrylonitrile (SAN), Molded
- Chi Mei Kibisan® PN-127H SAN
Chi Mei Kibisan® PN-127H SAN
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Kibisan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Kibisan® PN-127H SAN.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Chemical Resistant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Melt Flow | 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 6.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
6.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 | |
| 18 g/10 min @Load 10.0 kg, Temperature 220 °C |
18 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 | 85 | ASTM D787 |
| Ball Indentation Hardness | 164 MPa | 23800 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 77.0 MPa | 11200 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 7.0 % | 7.0 % | 50 mm/min; ISO 527 |
| Flexural Strength | 109 MPa | 15800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.70 GPa | 392 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 0.187 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.350 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D256 |
| 0.224 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
0.420 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | ISO 180/1C |
| Charpy Impact Unnotched | 2.40 J/cm² | 11.4 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179 |
| Impact | 3.00 | 3.00 | Impact Flexural Test Notched (KJ/m²) |
| 21.0 | 21.0 | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | unannealed; ISO 75 |
| 99.0 °C | 210 °F | annealed; ISO 75 | |
| Vicat Softening Point | 104 °C @Load 5.00 kg |
219 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 104 °C @Load 5.00 kg |
219 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 108 °C @Load 1.00 kg |
226 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 110 °C @Load 1.00 kg |
230 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- Polymer Resources NY6-G50 Nylon 6, 50% Glass Reinforced
- SABIC Innovative Plastics Lexan® 3262R PC (Asia Pacific)
- SABIC Innovative Plastics LNP Thermocomp DF008P PC
- Solvay ALKAMULS® STO-UNBL Surfactant
- Sumitomo Bakelite North America FS-10-VO-P Short-Glass Reinforced Diallyl Phthalate
- SABIC Innovative Plastics LNP VERTON RX07013 PA 66 (Europe-Africa-Middle East)
- TIMCAL TIMREX® SFG44 Primary Synthetic Graphite
- Goodfellow Titanium 88/Aluminum 12 Alloy
- SABIC Innovative Plastics LNP VERTON MV008SXP PP (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved