PTS Tristar® PC-10FR-(VIK) 16 MFI Flame Retardant, UV Stabilized Polycarbonate With Impact Modifier and Release

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified
Manufacturer Polymer Technology & Services, LLC (PTS)
Trade Name Tristar®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PTS Tristar® PC-10FR-(VIK) 16 MFI Flame Retardant, UV Stabilized Polycarbonate With Impact Modifier and Release.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ASTM D792
Water Absorption 0.18 %
0.18 %
24 Hrs; ASTM D570
Melt Flow 16 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 16 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM 1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength, Yield 55.2 MPa

@Thickness 3.17 mm
 8000 psi

@Thickness 0.125 in
 ASTM D638
Elongation at Break 75 %

@Thickness 3.17 mm
 75 %

@Thickness 0.125 in
 ASTM D638
Flexural Yield Strength 86.2 MPa

@Thickness 3.17 mm
 12500 psi

@Thickness 0.125 in
 ASTM D790
Flexural Modulus 2.07 GPa

@Thickness 3.17 mm
 300 ksi

@Thickness 0.125 in
 ASTM D790
Izod Impact, Notched 6.41 J/cm

@Thickness 3.17 mm
 12.0 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.2 µm/m-°C

@Temperature -40.0 - 95.0 °C
 39.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E831-06
CTE, linear, Transverse to Flow 68.4 µm/m-°C

@Temperature -40.0 - 95.0 °C
 38.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E831-06
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648
137 °C
279 °F
ISO 75
UL RTI, Electrical 125 °C
257 °F
UL RTI, Mechanical with Impact 115 °C
239 °F
UL RTI, Mechanical without Impact 125 °C
257 °F
Flammability, UL94 V-1

@Thickness 1.50 mm
 V-1

@Thickness 0.0591 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
Oxygen Index 36.9 %
36.9 %
ASTM D2863
Glow Wire Test 960 °C
1760 °F
GWFI; IEC 695-2-1/2
Electrical Properties Metric English Comments
Volume Resistivity 3.00e+15 ohm-cm
3.00e+15 ohm-cm
96 hours at 90°C; 50% RH; ASTM D257
6.00e+15 ohm-cm
6.00e+15 ohm-cm
40 hours; 23C; 50% RH; ASTM D257
Dielectric Strength 24.0 kV/mm

@Thickness 3.17 mm
 610 kV/in

@Thickness 0.125 in
 ASTM D149
Arc Resistance 60 - 120 sec
60 - 120 sec
PLC 6
High Voltage Arc Resistance to Ignition (HVAR) 16 sec

@Thickness 1.60 mm
 16 sec

@Thickness 0.0630 in
 UL 746A
Comparative Tracking Index 250 - 400 V
250 - 400 V
PLC 2
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness 1.50 mm
 15 - 30 sec

@Thickness 0.0591 in
 PLC 3
30 - 60 sec

@Thickness 3.00 mm
 30 - 60 sec

@Thickness 0.118 in
 PLC 2
High Amp Arc Ignition, HAI 60 - 120 arcs

@Thickness 3.00 mm
 60 - 120 arcs

@Thickness 0.118 in
 PLC 1
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 PLC 0
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
PLC 3