Eurostar Staramide AG4 PA66, 20% Glass Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide AG4 PA66, 20% Glass Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AG4 is a 20% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 5.5 % @Temperature 23.0 °C |
5.5 % @Temperature 73.4 °F |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | on Tensile Bar; ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 112 | 112 | ISO 2039-2 |
| Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 7.00 GPa | 1020 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.80 GPa | 986 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature -40.0 °C |
1.90 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1A | |
| 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | Edgew 80x10x4; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 31.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
17.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 95.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
52.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Af |
| Vicat Softening Point | 255 °C | 491 °F | B/120; ISO 306 |
| UL RTI, Electrical | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
IEC 60695-11-10 |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
IEC 60695-11-10 | |
| Flame Spread | 5.00 mm/min @Thickness 3.00 mm |
0.197 in/min @Thickness 0.118 in |
FMVSS Buring Speed |
| 10.0 mm/min @Thickness 2.00 mm |
0.394 in/min @Thickness 0.0787 in |
FMVSS Buring Speed | |
| Oxygen Index | 27 % | 27 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.4 @Frequency 50.0 - 60.0 Hz |
3.4 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 19.0 kV/mm @Thickness 3.20 mm |
483 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0068 @Frequency 50.0 - 60.0 Hz |
0.0068 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 450 V | 450 V | M; IEC 60112 |
| 550 V | 550 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 280 °C | 500 - 536 °F | Zone 1 |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | Zone 2 |
| Front Barrel Temperature | 270 - 290 °C | 518 - 554 °F | Zone 3 |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Moisture Content | 0.20 % | 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UL f1 | f1 |
Users viewing this material also viewed the following:
- RheTech Products T20P252-00 20% Talc Reinforced Polypropylene, Natural
- Polymer Resources TP-HG40 Polybutylene Terephthalate, 40% Glass Reinforced Alloy
- Global PC-FR2-U-CL-902 UL Recognized 94V-2 PC
- SABIC Innovative Plastics LNP Lubricomp WBG16 PBT (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP QF00A PA 6/10 (Europe-Africa-Middle East)
- A. Schulman PP 2175 Polypropylene High Flow Copolymer Polypropylene
- Clariant Renol PA113G15 Nylon 66, 15% Glass Fiber
- Eurotec® Tecodur® PB70 GR10 NL PBT 10% glass fiber reinforced
- Resinlab® TL5043 Anaerobic Threadlocking Compound
Copyright © lookpolymers.com All Rights Reserved