Overview of materials for Nylon 66, Nucleated

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Nucleated
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 66, Nucleated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Nucleated". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
Average value: 1.14 g/cc Grade Count:16
Water Absorption 1.20 - 1.50 %
1.20 - 1.50 %
Average value: 1.28 % Grade Count:11
Moisture Absorption at Equilibrium 2.00 - 2.40 %
2.00 - 2.40 %
Average value: 2.32 % Grade Count:5
Water Absorption at Saturation 8.50 %
8.50 %
Average value: 8.50 % Grade Count:3
Linear Mold Shrinkage 0.0100 - 0.0200 cm/cm
0.0100 - 0.0200 in/in
Average value: 0.0143 cm/cm Grade Count:14
Linear Mold Shrinkage, Transverse 0.0160 cm/cm
0.0160 in/in
Average value: 0.0160 cm/cm Grade Count:4
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105 - 109
105 - 109
Average value: 106 Grade Count:3
Tensile Strength, Ultimate 50.0 - 90.0 MPa
7250 - 13100 psi
Average value: 73.5 MPa Grade Count:7
Tensile Strength, Yield 60.0 - 95.0 MPa
8700 - 13800 psi
Average value: 81.6 MPa Grade Count:13
Elongation at Break 7.00 - 60.0 %
7.00 - 60.0 %
Average value: 27.7 % Grade Count:15
Elongation at Yield 3.80 - 40.0 %
3.80 - 40.0 %
Average value: 12.6 % Grade Count:7
Modulus of Elasticity 2.50 - 3.80 GPa
363 - 551 ksi
Average value: 3.12 GPa Grade Count:5
Flexural Yield Strength 35.0 - 138 MPa
5080 - 20000 psi
Average value: 110 MPa Grade Count:15
29.9922 - 29.9922 MPa

@Temperature 90.0 - 90.0 °C
4350.01 - 4350.01 psi

@Temperature 194 - 194 °F
Average value: 30.0 MPa Grade Count:1
Flexural Modulus 1.30 - 3.25 GPa
189 - 471 ksi
Average value: 2.75 GPa Grade Count:16
Izod Impact, Notched 0.400 - 0.587 J/cm
0.749 - 1.10 ft-lb/in
Average value: 0.503 J/cm Grade Count:9
Izod Impact, Notched (ISO) 3.99 - 15.0 kJ/m²
1.90 - 7.14 ft-lb/in²
Average value: 8.00 kJ/m² Grade Count:7
3.00 - 5.00 kJ/m²

@Temperature -40.0 - -20.0 °C
1.43 - 2.38 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 4.25 kJ/m² Grade Count:6
Charpy Impact Unnotched 27.0 J/cm² - NB
128 ft-lb/in² - NB
Average value: 27.0 J/cm² Grade Count:7
10.0 - 999.9 J/cm²

@Temperature -30.0 - -30.0 °C
47.6 - 4759 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 10.0 J/cm² Grade Count:5
Charpy Impact, Notched 0.500 - 1.50 J/cm²
2.38 - 7.14 ft-lb/in²
Average value: 0.867 J/cm² Grade Count:6
0.300 - 0.500 J/cm²

@Temperature -30.0 - -30.0 °C
1.43 - 2.38 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 0.447 J/cm² Grade Count:6
Thermal Properties Metric English Comments
CTE, linear 10.0 - 80.0 µm/m-°C
5.56 - 44.4 µin/in-°F
Average value: 57.5 µm/m-°C Grade Count:7
CTE, linear, Transverse to Flow 10.0 - 80.0 µm/m-°C
5.56 - 44.4 µin/in-°F
Average value: 33.3 µm/m-°C Grade Count:3
Melting Point 254 - 260 °C
489 - 500 °F
Average value: 257 °C Grade Count:5
Deflection Temperature at 0.46 MPa (66 psi) 210 - 237 °C
410 - 459 °F
Average value: 230 °C Grade Count:9
Deflection Temperature at 1.8 MPa (264 psi) 72.2 - 90.6 °C
162 - 195 °F
Average value: 83.6 °C Grade Count:14
UL RTI, Electrical 65.0 - 130 °C
149 - 266 °F
Average value: 122 °C Grade Count:3
UL RTI, Mechanical with Impact 65.0 - 75.0 °C
149 - 167 °F
Average value: 73.8 °C Grade Count:3
UL RTI, Mechanical without Impact 65.0 - 85.0 °C
149 - 185 °F
Average value: 81.3 °C Grade Count:3
Flammability, UL94 HB - V-2
HB - V-2
Grade Count:7
Oxygen Index 26.0 %
26.0 %
Average value: 26.0 % Grade Count:3
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+10 - 1.00e+18 ohm-cm
1.00e+10 - 1.00e+18 ohm-cm
Average value: 1.68e+17 ohm-cm Grade Count:6
Dielectric Strength 16.0 - 26.0 kV/mm
406 - 660 kV/in
Average value: 19.8 kV/mm Grade Count:9
Comparative Tracking Index 600 V
600 V
Average value: 600 V Grade Count:6
Processing Properties Metric English Comments
Nozzle Temperature 263 - 300 °C
505 - 572 °F
Average value: 281 °C Grade Count:5
Melt Temperature 241 - 304 °C
465 - 580 °F
Average value: 276 °C Grade Count:8
Mold Temperature 26.7 - 95.0 °C
80.0 - 203 °F
Average value: 76.1 °C Grade Count:6
Drying Temperature 70.0 - 85.0 °C
158 - 185 °F
Average value: 75.0 °C Grade Count:6
Injection Pressure 4.96 - 138 MPa
720 - 20000 psi
Average value: 43.2 MPa Grade Count:3