- Polycarbonate/ASA Alloy, Unreinforced
- Diamond Polymers ASA/PC TA-35
Diamond Polymers ASA/PC TA-35
| Category | Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ASA/PC TA-35.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ASA Weatherable Polymer, Injection Molding Grade, Very High ImpactInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 7.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
7.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ASTM D785 |
| Tensile Strength, Yield | 54.23 MPa | 7866 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.41 GPa | 350 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
10.0 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 98.3 °C | 209 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| Vicat Softening Point | 130 °C | 266 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 229 - 260 °C | 445 - 500 °F | |
| Middle Barrel Temperature | 232 - 266 °C | 450 - 510 °F | |
| Front Barrel Temperature | 235 - 271 °C | 455 - 520 °F | |
| Nozzle Temperature | 221 - 271 °C | 430 - 520 °F | |
| Melt Temperature | 221 - 271 °C | 430 - 520 °F | Melt temperatures above 530°F are not recommended, and may result in color shifts and or thermal instability. |
| Mold Temperature | 37.8 - 82.2 °C | 100 - 180 °F | Higher mold temperature can aid flow in processing, provides a better surface finish, and creates less residual stress in the finished products. |
| Drying Temperature | 90.6 - 98.9 °C | 195 - 210 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | <= 0.10 % | <= 0.10 % | |
| Back Pressure | 0.517 - 1.03 MPa | 75.0 - 150 psi |
Users viewing this material also viewed the following:
- Rogers Corporation Bisco™ HT-820 Cellular Silicone Foam
- Lehmann & Voss LUVOCOM® 20-7868 Polyphthalamide, with carbon fiber and glass fiber
- Ineos ABS Lustran® SAN DN77 SAN Grade
- Toyobo VYLOPET® EMC310TU Injection Molding Polyester Resin, Warpageless, High cycles
- Denka VINYKON W7080 PVC, W grade for non-migratory sheath and special items
- DuPont Teijin Films Mylar® LBT-2 Polyester Packaging Film, 48 Gauge
- Abatron AboCast/AboCure 50-24/8501-4 High Temperature Resistant Epoxy
- Aremco Lamp-Coat™ LC4010-GL High Temperature Coating, Silicone
- Axiall 22900 Coax & Telecom Flexible PVC
- SABIC Innovative Plastics Noryl FXN119LG PPE+HIPS (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved