LG Chemical LUPOY SC1004A PC

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer LG Chemical
Trade Name LUPOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOY SC1004A PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PC, General Purpose, High Toughness, Chemical resistance, High Impact (at Low Temperature)Application: Mobile Phone HousingCAS: 103598-77-2 and 143106-82-5Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 12 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 12 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 117
117
ASTM D785
Tensile Strength, Yield 55.9 MPa

@Thickness 3.20 mm
 8110 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 130 %

@Thickness 3.20 mm
 130 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 88.3 MPa

@Thickness 3.20 mm
 12800 psi

@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 2.06 GPa

@Thickness 3.20 mm
 299 ksi

@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched >= 5.39 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
 >= 10.1 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
 ASTM D256
>= 6.86 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 >= 12.9 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 130 °C

@Thickness 6.40 mm
 266 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 80.0 °C

@Thickness >=0.700 mm
 176 °F

@Thickness >=0.0276 in
UL RTI, Mechanical with Impact 80.0 °C

@Thickness >=0.700 mm
 176 °F

@Thickness >=0.0276 in
UL RTI, Mechanical without Impact 80.0 °C

@Thickness >=0.700 mm
 176 °F

@Thickness >=0.0276 in
Flammability, UL94 HB

@Thickness >=0.700 mm
 HB

@Thickness >=0.0276 in
Processing Properties Metric English Comments
Rear Barrel Temperature 275 - 290 °C
527 - 554 °F
Injection Molding
Middle Barrel Temperature 285 - 305 °C
545 - 581 °F
Injection Molding
Front Barrel Temperature 290 - 310 °C
554 - 590 °F
Injection Molding
Nozzle Temperature 285 - 305 °C
545 - 581 °F
Injection Molding
Melt Temperature 290 - 310 °C
554 - 590 °F
Injection Molding
Mold Temperature 80.0 - 110 °C
176 - 230 °F
Injection Molding
Drying Temperature 100 - 110 °C
212 - 230 °F
Injection Molding
Dry Time 3.00 - 5.00 hour
3.00 - 5.00 hour
Injection Molding
Back Pressure 0.981 - 3.92 MPa
142 - 569 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding