Firestone CR212-203-D Nylon 6, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Heat Stabilized |
| Manufacturer | Firestone |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Firestone CR212-203-D Nylon 6, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Black color. Heat stabilized, Modified, and Lubricated. Chip size is 2 x 3 mm.Information provided by Firestone
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Viscosity Measurement | 2.6 | 2.6 | Relative Viscosity; Sulfuric Acid |
| 46 | 46 | Relative Viscosity; Formic Acid | |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 79.0 MPa | 11500 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Flexural Yield Strength | 97.0 MPa | 14100 psi | ASTM D790 |
| Flexural Modulus | 2.59 GPa | 376 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 238 - 249 °C | 460 - 480 °F | |
| Middle Barrel Temperature | 238 - 249 °C | 460 - 480 °F | |
| Front Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Nozzle Temperature | 249 - 260 °C | 480 - 500 °F | |
| Melt Temperature | 249 - 260 °C | 480 - 500 °F | |
| Mold Temperature | 48.9 - 82.2 °C | 120 - 180 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- LATI Laticonther 92 GR/65 PUR, 65% Graphite Reinforced
- Solvay Specialty Polymers Ixef® DW-1022 Polyarylamide (PARA), 50% Glass Fiber (Dry)
- SABIC Innovative Plastics Valox® SHF4340 PBT (Europe-Africa-Middle East)
- SK Chemicals SKYTHANE® 168D S series Polyurethane
- Sawbones Laminated Test Blocks
- Covestro Bayfill® 370 Polyurethane Semi-Rigid Foam, Polymeric Catalyst, Closed Pour, MDI-based 2-Component Liquid System
- Esstech X-945-7446 Tetraethyleneglycol Dimethacrylate, C16H26O7
- 3M FV362 Soft Yellow Vinyl Label Products
- Arlon 55586R040 0.040" (1.02 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved