Overview of materials for Nylon 66, 20% Mineral Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Mineral Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 66, 20% Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Mineral Filled". Specific grades with primary filler content between 15% and 24% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.20 - 1.32 g/cc
0.0434 - 0.0477 lb/in³
Average value: 1.26 g/cc Grade Count:23
1.09 - 1.09 g/cc

@Temperature 295 - 295 °C
0.0394 - 0.0394 lb/in³

@Temperature 563 - 563 °F
Average value: 1.09 g/cc Grade Count:1
Filler Content 18.0 - 20.0 %
18.0 - 20.0 %
Average value: 19.6 % Grade Count:5
Water Absorption 0.500 - 7.70 %
0.500 - 7.70 %
Average value: 2.13 % Grade Count:11
Moisture Absorption at Equilibrium 2.00 - 2.50 %
2.00 - 2.50 %
Average value: 2.17 % Grade Count:6
Linear Mold Shrinkage 0.00200 - 0.0250 cm/cm
0.00200 - 0.0250 in/in
Average value: 0.0118 cm/cm Grade Count:23
Linear Mold Shrinkage, Transverse 0.0137 - 0.0141 cm/cm
0.0137 - 0.0141 in/in
Average value: 0.0139 cm/cm Grade Count:3
Melt Flow 3.00 - 25.0 g/10 min
3.00 - 25.0 g/10 min
Average value: 10.3 g/10 min Grade Count:3
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115 - 122
115 - 122
Average value: 119 Grade Count:6
Tensile Strength, Ultimate 50.0 - 93.0 MPa
7250 - 13500 psi
Average value: 70.0 MPa Grade Count:17
40.0 - 100 MPa

@Temperature -40.0 - 80.0 °C
5800 - 14500 psi

@Temperature -40.0 - 176 °F
Average value: 71.0 MPa Grade Count:1
Tensile Strength, Yield 70.0 - 95.0 MPa
10200 - 13800 psi
Average value: 83.1 MPa Grade Count:6
Elongation at Break 1.00 - 50.0 %
1.00 - 50.0 %
Average value: 10.2 % Grade Count:19
Modulus of Elasticity 1.49 - 6.60 GPa
217 - 957 ksi
Average value: 3.90 GPa Grade Count:12
0.398 - 4.827 GPa

@Temperature -40.0 - 150 °C
57.7 - 700.1 ksi

@Temperature -40.0 - 302 °F
Average value: 2.29 GPa Grade Count:1
Flexural Yield Strength 78.0 - 245 MPa
11300 - 35500 psi
Average value: 124 MPa Grade Count:18
57.0 - 160 MPa

@Temperature -40.0 - 80.0 °C
8270 - 23200 psi

@Temperature -40.0 - 176 °F
Average value: 113 MPa Grade Count:1
Flexural Modulus 2.50 - 6.60 GPa
363 - 957 ksi
Average value: 4.06 GPa Grade Count:17
1.60 - 6.40 GPa

@Temperature -40.0 - 80.0 °C
232 - 928 ksi

@Temperature -40.0 - 176 °F
Average value: 4.28 GPa Grade Count:1
Shear Modulus >= 0.0650 GPa

@Temperature -50.0 - 250 °C
>= 9.43 ksi

@Temperature -58.0 - 482 °F
Average value: 0.591 GPa Grade Count:1
Izod Impact, Notched 0.200 - 1.55 J/cm
0.375 - 2.90 ft-lb/in
Average value: 0.539 J/cm Grade Count:13
0.350 - 0.450 J/cm

@Temperature -40.0 - -40.0 °C
0.656 - 0.843 ft-lb/in

@Temperature -40.0 - -40.0 °F
Average value: 0.400 J/cm Grade Count:1
Izod Impact, Notched (ISO) 6.00 - 11.0 kJ/m²
2.86 - 5.23 ft-lb/in²
Average value: 8.13 kJ/m² Grade Count:3
8.00 - 8.00 kJ/m²

@Temperature -30.0 - -30.0 °C
3.81 - 3.81 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 8.00 kJ/m² Grade Count:1
Charpy Impact Unnotched 3.70 J/cm² - NB
17.6 ft-lb/in² - NB
Average value: 6.18 J/cm² Grade Count:6
1.00 - 4.30 J/cm²

@Temperature -20.0 - -20.0 °C
4.76 - 20.5 ft-lb/in²

@Temperature -4.00 - -4.00 °F
Average value: 2.65 J/cm² Grade Count:2
Charpy Impact, Notched 0.300 - 1.50 J/cm²
1.43 - 7.14 ft-lb/in²
Average value: 0.923 J/cm² Grade Count:7
0.100 - 1.20 J/cm²

@Temperature -30.0 - -20.0 °C
0.476 - 5.71 ft-lb/in²

@Temperature -22.0 - -4.00 °F
Average value: 0.500 J/cm² Grade Count:5
Thermal Properties Metric English Comments
CTE, linear 52.2 - 100 µm/m-°C
29.0 - 55.6 µin/in-°F
Average value: 70.1 µm/m-°C Grade Count:4
Melting Point 255 - 263 °C
491 - 505 °F
Average value: 259 °C Grade Count:11
Maximum Service Temperature, Air 80.0 - 220 °C
176 - 428 °F
Average value: 140 °C Grade Count:3
Deflection Temperature at 0.46 MPa (66 psi) 140 - 250 °C
284 - 482 °F
Average value: 218 °C Grade Count:17
Deflection Temperature at 1.8 MPa (264 psi) 75.0 - 230 °C
167 - 446 °F
Average value: 138 °C Grade Count:17
Vicat Softening Point 200 - 260 °C
392 - 500 °F
Average value: 233 °C Grade Count:5
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:16
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+10 - 1.00e+15 ohm-cm
1.00e+10 - 1.00e+15 ohm-cm
Average value: 4.40e+14 ohm-cm Grade Count:14
Surface Resistance 1.00e+10 - 1.00e+15 ohm
1.00e+10 - 1.00e+15 ohm
Average value: 1.70e+14 ohm Grade Count:6
Dielectric Constant 3.70 - 6.00
3.70 - 6.00
Average value: 4.38 Grade Count:4
Dielectric Strength 16.0 - 90.0 kV/mm
406 - 2290 kV/in
Average value: 40.0 kV/mm Grade Count:9
Comparative Tracking Index 450 - 600 V
450 - 600 V
Average value: 546 V Grade Count:6
Processing Properties Metric English Comments
Processing Temperature 270 - 310 °C
518 - 590 °F
Average value: 293 °C Grade Count:3
Melt Temperature 250 - 310 °C
482 - 590 °F
Average value: 285 °C Grade Count:13
Mold Temperature 49.0 - 120 °C
120 - 248 °F
Average value: 86.3 °C Grade Count:15
Drying Temperature 71.0 - 110 °C
160 - 230 °F
Average value: 86.4 °C Grade Count:11
Moisture Content 0.150 - 0.200 %
0.150 - 0.200 %
Average value: 0.190 % Grade Count:5
Injection Pressure 30.0 - 124 MPa
4350 - 18000 psi
Average value: 87.0 MPa Grade Count:5